| Specification |
CAS No.: 7085-85-0;
Formula: C6h7no2;
EINECS: 230-391-5;
Bonding Function: Instant Adhesive;
Morphology: Solvent;
Application: Automobile, Construction, Woodworking, Footwear & Leather, Fiber & Garment, Packing, Super Glue for Shoes;
Material: Acrylic;
Classification: Room Curing;
Main Agent Composition: Ethyl-Cyanoacrylate;
Characteristic: Weatherablity and Waterproof;
Promoter Composition: Stabilizer;
Composition: Organic Material;
Color: Clear;
Shelf Life: 15 Months;
Viscosity: 40-60 Cps;
Strength: Over 10 MPa;
Curing Time: Less Than 5 Seconds;
Open Time: 30 Minutes;
Gross Weight (CTN): 9.6kgs;
Net Weight (CTN): 8.5 Kgs;
Volume (CTN): 0.035m3/CTN;
Package Size (CTN): 455*335*235mm;
|
CAS No.: Mixed;
Formula: Mixed;
Bonding Function: Other;
Morphology: Other;
Application: Automobile, Construction, Woodworking, Footwear & Leather, Fiber & Garment, Packing, Other;
Material: Epoxy;
Classification: Room Curing;
Main Agent Composition: Other;
Characteristic: Waterproof;
Promoter Composition: Other;
Composition: Organic Material;
Color: White;
OEM: Avaliable;
Cetificate: ISO, TUV;
Shelf Life: 12 Months;
Volume: 300ml;
Location: Tianjin, China (Mainland);
Market: DIY Market;
Type: Two Component Marble Glue;
Packing: Bottle;
Carton Type: Five Ply Master Carton;
Colour: Clear, White, Black, Beige;
Other Names: Stone Epoxy Sealant;
Main Raw Material: Polyster Resin;
Bran: Gns;
Feature: Fast Curing;
Apprication Area: Sanitary and Kitchen;
|
Bonding Function: Structural Adhesive;
Morphology: Black Paste;
Application: Automobile, Construction, Woodworking;
Material: Polyurethane;
Classification: Room Curing;
Main Agent Composition: Polyurethane Prepolymer;
Characteristic: High Viscosity, Use with Primer, Waterproofing;
Promoter Composition: Complexing Agent;
Composition: Organic Material;
Color: Black;
Appearance: Uniform Paste;
Density: 1.25 ± 0.05 Kg/L;
Tack-Free Time (23ºC, 50% Rh): 15 ~ 35 Min;
Rate of Cure (23 ºC, 50% Rh): ≥ 3 mm/24hrs;
Work Temperature: 5 ~ 35 ºC;
Shore a Hardness: ~ 60;
Tensile Strength: ≥ 6 N/mm^2;
Elongation at Break: ~ 300%;
Shear Strength: ≥ 4 N/mm^2;
Tear Strength: ≥ 10 N/mm;
|
Bonding Function: Structural Adhesive;
Morphology: Black Paste;
Application: Automobile, Construction, Woodworking;
Material: Polyurethane;
Classification: Room Curing;
Main Agent Composition: Polyurethane Prepolymer;
Characteristic: High Viscosity, Use with Primer, Waterproofing;
Promoter Composition: Complexing Agent;
Composition: Organic Material;
Color: Black;
Appearance: Uniform Paste;
Density: 1.25 ± 0.05 Kg/L;
Tack-Free Time (23ºC, 50% Rh): 15 ~ 35 Min;
Rate of Cure (23 ºC, 50% Rh): ≥ 3 mm/24hrs;
Work Temperature: 5 ~ 35 ºC;
Shore a Hardness: ~ 60;
Tensile Strength: ≥ 6 N/mm^2;
Elongation at Break: ~ 300%;
Shear Strength: ≥ 4 N/mm^2;
Tear Strength: ≥ 10 N/mm;
|
Bonding Function: Structural Adhesive;
Morphology: Black Paste;
Application: Automobile, Construction, Woodworking;
Material: Polyurethane;
Classification: Room Curing;
Main Agent Composition: Polyurethane Prepolymer;
Characteristic: High Viscosity, Use with Primer, Waterproofing;
Promoter Composition: Complexing Agent;
Composition: Organic Material;
Color: Black;
Appearance: Uniform Paste;
Density: 1.25 ± 0.05 Kg/L;
Tack-Free Time (23ºC, 50% Rh): 15 ~ 35 Min;
Rate of Cure (23 ºC, 50% Rh): ≥ 3 mm/24hrs;
Work Temperature: 5 ~ 35 ºC;
Shore a Hardness: ~ 60;
Tensile Strength: ≥ 6 N/mm^2;
Elongation at Break: ~ 300%;
Shear Strength: ≥ 4 N/mm^2;
Tear Strength: ≥ 10 N/mm;
|