| Specification |
Bonding Function: Instant Adhesive;
Morphology: Solvent;
Application: Automobile, Construction, Woodworking, Footwear & Leather, Fiber & Garment, Packing, DIY Plastic Repair;
Material: Acrylic;
Classification: Room Curing;
Main Agent Composition: Ethyl-Cyanoacrylate;
Characteristic: Weatherablity and Waterproof;
Promoter Composition: Stabilizer;
Color: Clear;
Shelf Life: 24 Months;
Viscosity: 40-60 Cps;
Strength: Over 10 MPa;
Curing Time: Less Than 5 Seconds;
Open Time: 30 Minutes;
Package Size (CTN): 352*350*365mm;
Gross Weight (CTN): 5 Kgs;
Net Weight (CTN): 4 Kgs;
Volume (CTN): 0.045 M2;
|
Bonding Function: Structural Adhesive;
Morphology: Black Paste;
Application: Automobile;
Material: Polyurethane;
Classification: Room Curing;
Main Agent Composition: Polyurethane Prepolymer;
Characteristic: High Viscosity, High Shear Strength, Fast Cure;
Promoter Composition: Complexing Agent;
Composition: Organic Material;
Color: Black;
Density: 1.20±0.05 Kg/L;
Cure Mechanism: Moisture-Curing;
Non-Sag Properties: Good;
Shore a Hardness: ~ 60;
Shear Strength: ≥ 5 N/mm^2;
Tensile Strength: ≥ 8 N/mm^2;
Elongation at Break: ≥ 400%;
Tear Strength: ≥ 10 N/mm;
Tack-Free Time (23 ºC , 50% Rh): 20~40 Min;
Rate of Cure (23 ºC, 50% Rh): ≥ 3.5 mm/24hrs;
|
Bonding Function: Structural Adhesive;
Morphology: Black Paste;
Application: Automobile;
Material: Polyurethane;
Classification: Room Curing;
Main Agent Composition: Polyurethane Prepolymer;
Characteristic: High Viscosity, High Shear Strength, Fast Cure;
Promoter Composition: Complexing Agent;
Composition: Organic Material;
Color: Black;
Density: 1.20±0.05 Kg/L;
Cure Mechanism: Moisture-Curing;
Non-Sag Properties: Good;
Shore a Hardness: ~ 60;
Shear Strength: ≥ 5 N/mm^2;
Tensile Strength: ≥ 8 N/mm^2;
Elongation at Break: ≥ 400%;
Tear Strength: ≥ 10 N/mm;
Tack-Free Time (23 ºC , 50% Rh): 20~40 Min;
Rate of Cure (23 ºC, 50% Rh): ≥ 3.5 mm/24hrs;
|
Bonding Function: Structural Adhesive;
Morphology: Black Paste;
Application: Automobile;
Material: Polyurethane;
Classification: Room Curing;
Main Agent Composition: Polyurethane Prepolymer;
Characteristic: High Viscosity, High Shear Strength, Fast Cure;
Promoter Composition: Complexing Agent;
Composition: Organic Material;
Color: Black;
Density: 1.20±0.05 Kg/L;
Cure Mechanism: Moisture-Curing;
Non-Sag Properties: Good;
Shore a Hardness: ~ 60;
Shear Strength: ≥ 5 N/mm^2;
Tensile Strength: ≥ 8 N/mm^2;
Elongation at Break: ≥ 400%;
Tear Strength: ≥ 10 N/mm;
Tack-Free Time (23 ºC , 50% Rh): 20~40 Min;
Rate of Cure (23 ºC, 50% Rh): ≥ 3.5 mm/24hrs;
|
Bonding Function: Structural Adhesive;
Morphology: Black Paste;
Application: Automobile;
Material: Polyurethane;
Classification: Room Curing;
Main Agent Composition: Polyurethane Prepolymer;
Characteristic: High Viscosity, High Shear Strength, Fast Cure;
Promoter Composition: Complexing Agent;
Composition: Organic Material;
Color: Black;
Density: 1.20±0.05 Kg/L;
Cure Mechanism: Moisture-Curing;
Non-Sag Properties: Good;
Shore a Hardness: ~ 60;
Shear Strength: ≥ 5 N/mm^2;
Tensile Strength: ≥ 8 N/mm^2;
Elongation at Break: ≥ 400%;
Tear Strength: ≥ 10 N/mm;
Tack-Free Time (23 ºC , 50% Rh): 20~40 Min;
Rate of Cure (23 ºC, 50% Rh): ≥ 3.5 mm/24hrs;
|