Specification |
Bonding Function: High Temperature Resistant Adhesive;
Morphology: Solvent;
Application: Automobile, Construction, Woodworking, Footwear & Leather, Fiber & Garment, Packing, Automobile Production of Bonding and Sealing;
Material: Silicone;
Classification: Room Curing;
Main Agent Composition: Natural Polymer;
Characteristic: Weatherablity and Waterproof;
Promoter Composition: Stabilizer;
Composition: Organic Material;
Color: Red/Grey/Black;
Ordor: Neutral;
24 Hour Cure Rate(mm): 2.93;
Surface Drying Time(Mins): 10;
Density(g/cm3): 1.43;
Elongation(%): 360;
Tensile Strength(MPa): 2.18;
Volatile(%): 4.2;
Hardness( Shore a ): 45;
Package Size (CTN): 415*250*360mm;
|
CAS No.: 95588-52-5;
EINECS: Mixture;
Bonding Function: Oil Level Adhesive;
Morphology: Solvent;
Application: Automobile, Construction, Woodworking, Footwear & Leather, Fiber & Garment, Packing, Decoration;
Material: Chloroprene Rubber;
Classification: Room Curing;
Main Agent Composition: Rubber;
Characteristic: Weatherability;
Promoter Composition: Solvent;
Composition: Inorganic Material;
Color: Yellow;
Solid Content: 23%;
Viscosity: 1800-3800cps at Normal Temperature;
Density: 0.88-1.1 Kg/L;
Initial Viscidity: 0.7 MPa;
Shear Strength: 1.7 MPa;
Tack Time: Around 15 Minutes to 60 Minutes;
Temperature Durability: up to 120 Celsius Degree;
Benzene: No More Than 0.1g/Kg;
Dissociative Formaldehyde: No More Than 0.37g/Kg;
Appearance: Yellow Light Liquid;
|
CAS No.: 95588-52-5;
EINECS: Mixture;
Bonding Function: Oil Level Adhesive;
Morphology: Solvent;
Application: Automobile, Construction, Woodworking, Footwear & Leather, Fiber & Garment, Packing, Decoration;
Material: Chloroprene Rubber;
Classification: Room Curing;
Main Agent Composition: Rubber;
Characteristic: Weatherability;
Promoter Composition: Solvent;
Composition: Inorganic Material;
Color: Yellow;
Solid Content: 23%;
Viscosity: 1800-3800cps at Normal Temperature;
Density: 0.88-1.1 Kg/L;
Initial Viscidity: 0.7 MPa;
Shear Strength: 1.7 MPa;
Tack Time: Around 15 Minutes to 60 Minutes;
Temperature Durability: up to 120 Celsius Degree;
Benzene: No More Than 0.1g/Kg;
Dissociative Formaldehyde: No More Than 0.37g/Kg;
Appearance: Yellow Light Liquid;
|
CAS No.: 95588-52-5;
EINECS: Mixture;
Bonding Function: Oil Level Adhesive;
Morphology: Solvent;
Application: Automobile, Construction, Woodworking, Footwear & Leather, Fiber & Garment, Packing, Decoration;
Material: Chloroprene Rubber;
Classification: Room Curing;
Main Agent Composition: Rubber;
Characteristic: Weatherability;
Promoter Composition: Solvent;
Composition: Inorganic Material;
Color: Yellow;
Solid Content: 23%;
Viscosity: 1800-3800cps at Normal Temperature;
Density: 0.88-1.1 Kg/L;
Initial Viscidity: 0.7 MPa;
Shear Strength: 1.7 MPa;
Tack Time: Around 15 Minutes to 60 Minutes;
Temperature Durability: up to 120 Celsius Degree;
Benzene: No More Than 0.1g/Kg;
Dissociative Formaldehyde: No More Than 0.37g/Kg;
Appearance: Yellow Light Liquid;
|
CAS No.: 95588-52-5;
EINECS: Mixture;
Bonding Function: Oil Level Adhesive;
Morphology: Solvent;
Application: Automobile, Construction, Woodworking, Footwear & Leather, Fiber & Garment, Packing, Decoration;
Material: Chloroprene Rubber;
Classification: Room Curing;
Main Agent Composition: Rubber;
Characteristic: Weatherability;
Promoter Composition: Solvent;
Composition: Inorganic Material;
Color: Yellow;
Solid Content: 23%;
Viscosity: 1800-3800cps at Normal Temperature;
Density: 0.88-1.1 Kg/L;
Initial Viscidity: 0.7 MPa;
Shear Strength: 1.7 MPa;
Tack Time: Around 15 Minutes to 60 Minutes;
Temperature Durability: up to 120 Celsius Degree;
Benzene: No More Than 0.1g/Kg;
Dissociative Formaldehyde: No More Than 0.37g/Kg;
Appearance: Yellow Light Liquid;
|