| Specification |
CAS No.: 7085-85-0;
Formula: C6h7no2;
EINECS: 230-391-5;
Bonding Function: Instant Adhesive;
Morphology: Solvent;
Application: Automobile, Construction, Woodworking, Footwear & Leather, Fiber & Garment, Packing, Bonding Difficult-to-Bond Substrates;
Material: Acrylic;
Classification: Room Curing;
Main Agent Composition: Ethyl-Cyanoacrylate;
Characteristic: Weatherablity and Waterproof;
Promoter Composition: Stabilizer;
Composition: Organic Material;
Color: Clear;
Shelf Life: 15 Months;
Viscosity: 10 0000 Cps;
Strength: Over 10 MPa;
Curing Time: 10-30 Seconds;
Open Time: 30 Minutes;
Product Size: 57*36*150mm;
Package Size (CTN): 352*330*365 mm;
Gross Weight (CTN): 4.5 Kgs;
Net Weight (CTN): 4.0 Kgs;
Volume (CTN): 0.042 M2;
|
Bonding Function: Structural Adhesive;
Morphology: Black Paste;
Application: Automobile;
Material: Polyurethane;
Classification: Room Curing;
Main Agent Composition: Polyurethane Prepolymer;
Characteristic: Fast Cure, High Shear Strength, Waterproofing;
Promoter Composition: Complexing Agent;
Composition: Organic Material;
Color: Black;
Density: 1.30±0.05 Kg/L;
Tack-Free Time (23 ºC, 50% Rh): 20~60 Min;
Rate of Cure (23 ºC, 50% Rh): ≥ 3 mm/24hrs;
Shore a Hardness: 60±5;
Shear Strength: ≥ 2 N/mm^2;
Tensile Strength: ≥ 5 N/mm^2;
Elongation at Break: ≥ 400%;
Tear Strength: ≥ 10 N/mm;
Non-Sag Properties: Good;
Shelf Life (Storage Below 25ºC): Cartridge:9 Months Sausage:6 Months;
|
Bonding Function: Structural Adhesive;
Morphology: Black Paste;
Application: Automobile;
Material: Polyurethane;
Classification: Room Curing;
Main Agent Composition: Polyurethane Prepolymer;
Characteristic: Fast Cure, High Shear Strength, Waterproofing;
Promoter Composition: Complexing Agent;
Composition: Organic Material;
Color: Black;
Density: 1.30±0.05 Kg/L;
Tack-Free Time (23 ºC, 50% Rh): 20~60 Min;
Rate of Cure (23 ºC, 50% Rh): ≥ 3 mm/24hrs;
Shore a Hardness: 60±5;
Shear Strength: ≥ 2 N/mm^2;
Tensile Strength: ≥ 5 N/mm^2;
Elongation at Break: ≥ 400%;
Tear Strength: ≥ 10 N/mm;
Non-Sag Properties: Good;
Shelf Life (Storage Below 25ºC): Cartridge:9 Months Sausage:6 Months;
|
Bonding Function: Structural Adhesive;
Morphology: Black Paste;
Application: Automobile;
Material: Polyurethane;
Classification: Room Curing;
Main Agent Composition: Polyurethane Prepolymer;
Characteristic: Fast Cure, High Shear Strength, Waterproofing;
Promoter Composition: Complexing Agent;
Composition: Organic Material;
Color: Black;
Density: 1.30±0.05 Kg/L;
Tack-Free Time (23 ºC, 50% Rh): 20~60 Min;
Rate of Cure (23 ºC, 50% Rh): ≥ 3 mm/24hrs;
Shore a Hardness: 60±5;
Shear Strength: ≥ 2 N/mm^2;
Tensile Strength: ≥ 5 N/mm^2;
Elongation at Break: ≥ 400%;
Tear Strength: ≥ 10 N/mm;
Non-Sag Properties: Good;
Shelf Life (Storage Below 25ºC): Cartridge:9 Months Sausage:6 Months;
|
Bonding Function: Structural Adhesive;
Morphology: Black Paste;
Application: Automobile;
Material: Polyurethane;
Classification: Room Curing;
Main Agent Composition: Polyurethane Prepolymer;
Characteristic: Fast Cure, High Shear Strength, Waterproofing;
Promoter Composition: Complexing Agent;
Composition: Organic Material;
Color: Black;
Density: 1.30±0.05 Kg/L;
Tack-Free Time (23 ºC, 50% Rh): 20~60 Min;
Rate of Cure (23 ºC, 50% Rh): ≥ 3 mm/24hrs;
Shore a Hardness: 60±5;
Shear Strength: ≥ 2 N/mm^2;
Tensile Strength: ≥ 5 N/mm^2;
Elongation at Break: ≥ 400%;
Tear Strength: ≥ 10 N/mm;
Non-Sag Properties: Good;
Shelf Life (Storage Below 25ºC): Cartridge:9 Months Sausage:6 Months;
|