Specification |
Material: Acrylic;
Water Absorption: 0.2%~0.3%;
Contraction Percentage: <0.4%;
Tensile Strength: 51~80MPa;
Thickness: 2mm, 3mm, 4mm, up to 60mm;
Application: Advertising, Signs, Decoration, Construion;
Density: 1.2g/cm3;
Type: Cast Acrylic Sheet;
Surface: Gloss, Matte(Frosted, Satin);
Raw Material: 100% Virgin MMA;
Other Name: PMMA Sheet;
|
After-sales Service: Yes;
Warranty: 1 Year;
Material: Mc Nylon;
Kind: Engineering Plastic Sheet;
Water Absorption: <0.01%;
Contraction Percentage: 2.0%~5.0%;
Tensile Strength: 81~130MPa;
Color: Milk White/Blue;
Name: Mc Nylon Guide Sheet Rail and Parts;
Feature: High Abrasion Resistant;
|
After-sales Service: 1 Year;
Warranty: 1 Year;
Material: PE;
Kind: Hard Plastic Sheet;
Water Absorption: <0.01%;
Contraction Percentage: 2.0%~5.0%;
Tensile Strength: 41~50MPa;
Color: Customized;
Thickness: 3mm-300mm;
Density: 0.94-0.97g/Cm³;
Hardness: Shore D 62-68;
Surface: Smooth / Gross;
|
After-sales Service: 10 Years;
Warranty: 3 Years;
Material: PVC;
Kind: PVC Plastic Sheet;
Water Absorption: <0.01%;
Contraction Percentage: <0.4%;
Tensile Strength: 81~130MPa;
Thickness: 3-30mm;
Density: 0.4-0.9g/cm3;
Application: Decoration Parts, Structural Components, Functiona;
Color: Multi Color;
Forming Way: Extrusion;
Material Properties: Flame Retardant;
Surface Finishing: Finished;
Delivery Time: 7-10 Days After Confirmed Customers′ Deposit;
MOQ: 50PCS for Each Color;
Feature: Strong&Durable, Hard&Rigid, Non-Toxic;
Flame Retardence: Self-Extinguishing Less Than 5 Seconds;
Foam Process: Celuka, Extrude, Hardness Surface;
Processing Effect: The Edge Smooth After Cut by CNC;
|
After-sales Service: Replace;
Warranty: 7 Years;
Material: PE;
Kind: Engineering Plastic Sheet;
Water Absorption: <0.01%;
Contraction Percentage: 2.0%~5.0%;
Tensile Strength: 30~40MPa;
Density: 0.93~0.96;
Standard Color: Black, White, Red, Yellow and Others;
Customied Logo: Available;
Surface: Self-Lubricating and Anti-Slip Pattern;
Shape: Customized;
Logo: Available;
Coefficient of Friction: 0.12-0.15;
Elongation at Break: 300%-500%;
|