Specification |
After-sales Service: 1 Year;
Warranty: 1 Year;
Material: Acrylic;
Kind: Color Plastic Sheet;
Water Absorption: 0.2%~0.4%;
Contraction Percentage: <0.4%;
Tensile Strength: 51~80MPa;
Jumei Quality: World-Class Acrylic Sheets Manufacturer;
Company Manufacturing History: More Than 20 Years;
Thickness Tolerance: +-0.3;
Model No.: Jm Acrylic Mirror Sheet/PMMA Mirror Sheets;
Density: 1.2g/cm3;
Thickness: 0.8, 1, 1.5, 1.8, 2, 2.5, 2.8, 3mm (0.8-5mm);
Color: Color: Silver, Gold, Rose Gold, Blue, Red, Bronze;
Sizes: 1220*1830mm, 1220*2440mm, 1020*2020 mm;
Backside: Painting and Adhesive;
Engineer Team: From Taiwan;
Production Lines: Full-Automatic Production Lines, Dust-Free Worksho;
Equipment: Imported Glass Models (From Pilkington Glass in U.;
Main Market: We Export to 120 Countries Around The World;
Application: Decoration, Advertising, Display, Handcrafts etc.;
|
Material: EPDM Foam, Cr Foam, EVA Foam;
Kind: Color Plastic Sheet;
Water Absorption: <0.01%;
Contraction Percentage: 22.7%;
Tensile Strength: 0.44MPa;
Foam Type: Closed Cell EPDM Foam;
Density: 110-150kg/M3;
Elongation: 316%;
Elongation Rate of Change: 3.5%;
Heat Shrinkage: 0.8%;
Thickness: 1-50mm;
Application: Packing, Automobile;
Sample Foam: Available;
|
Material: NBR/PVC, Open Cell EPDM Foam;
Kind: Color Plastic Sheet;
Water Absorption: <0.01%;
Contraction Percentage: 2.0%~5.0%;
Tensile Strength: 3.46MPa;
Foam Type: Closed Cell EPDM Foam;
Density: 110-150kg/M3;
Elongation: 316%;
Elongation Rate of Change: 3.5%;
Heat Shrinkage: 0.8%;
Thickness: 1-50mm;
Buring Speed: 50mm/Min;
Application: Packing, Automotive;
Sample Foam: Avaliable;
Delivery Time: in 2-3 Weeks;
|
Material: PVC;
Kind: PVC Plastic Sheet;
Water Absorption: <0.01%;
Contraction Percentage: <0.4%;
Tensile Strength: 81~130MPa;
Color: Natural, Light Blue or as Required;
Name: PVC Sheet;
Character: Super Clear, Smooth;
Thickness: 0.1mm-10mm;
Width: 100-2000mm;
Bubble: No;
Open Styles: Swing;
|
Material: EPDM, Cr, EVA;
Kind: Color Plastic Sheet;
Water Absorption: <0.01%;
Contraction Percentage: 2.0%~5.0%;
Tensile Strength: 3.46MPa;
Denstiy: 110-150kgs/M3;
Hardness Shore C: 8-25;
Tensile: >3MPa;
Elongation: >120%;
Tearing Strength: 260n/M;
Compression Strength: >30+/-10kpa;
Dimensional Change: <3.2%;
Thermal Conductivity: <0.038W/M.K;
Absorbent: <0.04kg/Cm2;
Buring Speed: 50mm/Min;
|