| Specification |
CAS No.: 7085-85-0;
Formula: Mixture;
EINECS: 230-391-5;
Bonding Function: Structural Adhesive;
Morphology: Solvent;
Application: Construction, Woodworking;
Material: Silicone;
Classification: Room Curing;
Main Agent Composition: Polydimethylsiloxane;
Characteristic: Waterproof;
Promoter Composition: Plasticizer;
Composition: Organic Material;
Color: Clear;
Feature 1: Fast Dry;
Feature 2: No Toxic;
Feature 3: Extrusion Smooth;
Feature 4: Free of Impurities;
Certificates: ISO 9001, ISO 14001, ISO 50001, SGS, TUV;
Property: Aceoxy;
Shelf Life: 3-20 Years;
Useage: Glass, Aluminum, Fish Tank, General Purpose;
Price: Competitive;
Factroy: 5 Factories;
Industry: Construction, Home Decoration, Silicone Oil;
OEM: Yes;
Ability: Weatherproof, Waterproof;
Colors: Black, White, Grey, OEM Colorful;
|
Bonding Function: Structural Adhesive;
Morphology: Black Paste;
Application: Automobile, Construction, Woodworking;
Material: Polyurethane;
Classification: Room Curing;
Main Agent Composition: Polyurethane Prepolymer;
Characteristic: High Viscosity, Use with Primer, Waterproofing;
Promoter Composition: Complexing Agent;
Composition: Organic Material;
Color: Black;
Appearance: Uniform Paste;
Density: 1.25 ± 0.05 Kg/L;
Tack-Free Time (23ºC, 50% Rh): 15 ~ 35 Min;
Rate of Cure (23 ºC, 50% Rh): ≥ 3 mm/24hrs;
Work Temperature: 5 ~ 35 ºC;
Shore a Hardness: ~ 60;
Tensile Strength: ≥ 6 N/mm^2;
Elongation at Break: ~ 300%;
Shear Strength: ≥ 4 N/mm^2;
Tear Strength: ≥ 10 N/mm;
|
Bonding Function: Structural Adhesive;
Morphology: Black Paste;
Application: Automobile, Construction, Woodworking;
Material: Polyurethane;
Classification: Room Curing;
Main Agent Composition: Polyurethane Prepolymer;
Characteristic: High Viscosity, Use with Primer, Waterproofing;
Promoter Composition: Complexing Agent;
Composition: Organic Material;
Color: Black;
Appearance: Uniform Paste;
Density: 1.25 ± 0.05 Kg/L;
Tack-Free Time (23ºC, 50% Rh): 15 ~ 35 Min;
Rate of Cure (23 ºC, 50% Rh): ≥ 3 mm/24hrs;
Work Temperature: 5 ~ 35 ºC;
Shore a Hardness: ~ 60;
Tensile Strength: ≥ 6 N/mm^2;
Elongation at Break: ~ 300%;
Shear Strength: ≥ 4 N/mm^2;
Tear Strength: ≥ 10 N/mm;
|
Bonding Function: Structural Adhesive;
Morphology: Black Paste;
Application: Automobile, Construction, Woodworking;
Material: Polyurethane;
Classification: Room Curing;
Main Agent Composition: Polyurethane Prepolymer;
Characteristic: High Viscosity, Use with Primer, Waterproofing;
Promoter Composition: Complexing Agent;
Composition: Organic Material;
Color: Black;
Appearance: Uniform Paste;
Density: 1.25 ± 0.05 Kg/L;
Tack-Free Time (23ºC, 50% Rh): 15 ~ 35 Min;
Rate of Cure (23 ºC, 50% Rh): ≥ 3 mm/24hrs;
Work Temperature: 5 ~ 35 ºC;
Shore a Hardness: ~ 60;
Tensile Strength: ≥ 6 N/mm^2;
Elongation at Break: ~ 300%;
Shear Strength: ≥ 4 N/mm^2;
Tear Strength: ≥ 10 N/mm;
|
Bonding Function: Structural Adhesive;
Morphology: Black Paste;
Application: Automobile, Construction, Woodworking;
Material: Polyurethane;
Classification: Room Curing;
Main Agent Composition: Polyurethane Prepolymer;
Characteristic: High Viscosity, Use with Primer, Waterproofing;
Promoter Composition: Complexing Agent;
Composition: Organic Material;
Color: Black;
Appearance: Uniform Paste;
Density: 1.25 ± 0.05 Kg/L;
Tack-Free Time (23ºC, 50% Rh): 15 ~ 35 Min;
Rate of Cure (23 ºC, 50% Rh): ≥ 3 mm/24hrs;
Work Temperature: 5 ~ 35 ºC;
Shore a Hardness: ~ 60;
Tensile Strength: ≥ 6 N/mm^2;
Elongation at Break: ~ 300%;
Shear Strength: ≥ 4 N/mm^2;
Tear Strength: ≥ 10 N/mm;
|