| Specification |
Formula: Mixture;
Bonding Function: Structural Adhesive;
Morphology: Solvent;
Application: Construction, Woodworking, Window, Room;
Material: Silicone;
Classification: Room Curing;
Main Agent Composition: Polydimethylsiloxane;
Characteristic: Weatherproof, Waterproof;
Promoter Composition: Curing Agent, Plasticizer, Filler, Coupling Agent;
Composition: Organic Material;
Color: White, Black, Grey, Customizable;
Certificates: ISO 9001, ISO 14001, ISO 50001, SGS, TUV;
Feature 1: Fast Dry;
Feature 2: No Toxic;
Feature 3: Extrusion Smooth;
Feature 4: Free of Impurities;
|
CAS No.: C6h18osi2;
Formula: C6h7no2;
EINECS: 63148-62-9;
Bonding Function: Instant Adhesive;
Morphology: Solid-State;
Application: Construction, Woodworking, Footwear & Leather, Fiber & Garment, Packing, Construction, Fiber & Garment, Footwear & Leather;
Material: a:Epoxy Resin;B Sulfur Curing Agent;
Classification: Pressure-Sensitive;
Main Agent Composition: Ethyl Cyanoacrylate;
Characteristic: Double Components Glue;
Promoter Composition: Curing Agent;
Composition: Organic Material;
Color: White&Black for Both a and B;
Brand Name: Magpow;
Components Rate: a:B=1:1;
Curing Time: 20-25 Mins (25°c Mix Glue, 3-8g);
Shear Strength: ≥10MPa (25°*48h, Steel-Steel);
Stock: Full;
Custom-Tailor: Can Accept;
|
Bonding Function: Structural Adhesive;
Morphology: Black Paste;
Application: Automobile, Construction, Woodworking;
Material: Polyurethane;
Classification: Room Curing;
Main Agent Composition: Polyurethane Prepolymer;
Characteristic: High Viscosity, Use with Primer, Waterproofing;
Promoter Composition: Complexing Agent;
Composition: Organic Material;
Color: Black;
Appearance: Uniform Paste;
Density: 1.25 ± 0.05 Kg/L;
Tack-Free Time (23ºC, 50% Rh): 15 ~ 35 Min;
Rate of Cure (23 ºC, 50% Rh): ≥ 3 mm/24hrs;
Work Temperature: 5 ~ 35 ºC;
Shore a Hardness: ~ 60;
Tensile Strength: ≥ 6 N/mm^2;
Elongation at Break: ~ 300%;
Shear Strength: ≥ 4 N/mm^2;
Tear Strength: ≥ 10 N/mm;
|
Bonding Function: Structural Adhesive;
Morphology: Black Paste;
Application: Automobile, Construction, Woodworking;
Material: Polyurethane;
Classification: Room Curing;
Main Agent Composition: Polyurethane Prepolymer;
Characteristic: High Viscosity, Use with Primer, Waterproofing;
Promoter Composition: Complexing Agent;
Composition: Organic Material;
Color: Black;
Appearance: Uniform Paste;
Density: 1.25 ± 0.05 Kg/L;
Tack-Free Time (23ºC, 50% Rh): 15 ~ 35 Min;
Rate of Cure (23 ºC, 50% Rh): ≥ 3 mm/24hrs;
Work Temperature: 5 ~ 35 ºC;
Shore a Hardness: ~ 60;
Tensile Strength: ≥ 6 N/mm^2;
Elongation at Break: ~ 300%;
Shear Strength: ≥ 4 N/mm^2;
Tear Strength: ≥ 10 N/mm;
|
Bonding Function: Structural Adhesive;
Morphology: Black Paste;
Application: Automobile, Construction, Woodworking;
Material: Polyurethane;
Classification: Room Curing;
Main Agent Composition: Polyurethane Prepolymer;
Characteristic: High Viscosity, Use with Primer, Waterproofing;
Promoter Composition: Complexing Agent;
Composition: Organic Material;
Color: Black;
Appearance: Uniform Paste;
Density: 1.25 ± 0.05 Kg/L;
Tack-Free Time (23ºC, 50% Rh): 15 ~ 35 Min;
Rate of Cure (23 ºC, 50% Rh): ≥ 3 mm/24hrs;
Work Temperature: 5 ~ 35 ºC;
Shore a Hardness: ~ 60;
Tensile Strength: ≥ 6 N/mm^2;
Elongation at Break: ~ 300%;
Shear Strength: ≥ 4 N/mm^2;
Tear Strength: ≥ 10 N/mm;
|