| Specification |
Refractoriness (℃): 1770< Refractoriness< 2000;
Feature: Long Time Materials;
Type: Refractory Material;
Shape: Brick;
Material: Fireclay;
Al2O3: Min40%;
Application: Pizza Oven;
Brick: Firecaly Brick;
Refractory Material: The Furnace Lining Material;
High Alumina Brick: Fireclay Brick;
|
Classification: Magnesia-Chrome Brick;
Refractoriness (℃): 1580< Refractoriness< 1770, 1770< Refractoriness< 2000;
Shape: Brick, Brick;
Feature: Long Time Materials;
Type: Refractory Material;
Material: MGO-Carbon Brick;
Application Limit Temp: 1700c;
Apparent Porosity: 16-18%;
Bulk Density: 2.95-3.15g/cm3;
Cold Crushing Strength: 40MPa;
Thermal Shock Resistance @950c Air Cool: 40times;
Refractoriness Under [email protected]: 1650-1700c;
MGO: 55-75%;
Cr2o3: 8-22%;
Sio2: 2.0-2.5;
|
Feature: Good Acid Resistance, Good Mechanical Strength, High Refractoriness, Low Thermal Conductivity, Permeability, Thermal Shock Resistance;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Plate, Board;
Usage: High Temperature Insulating Material;
Temprature Classification: 1050℃;
Manufacturing Technique: Stirring, Heating, Gelling, Forming, Drying;
Kind: Reinforcing Fiber;
Chemical Composition: Sio2+Cao;
Size: Customizable;
Certifiacte: ISO9001, CE, etc;
Working Temp: 1000c;
Bulk Density: 250kg/M3;
Compressive Strength: 0.52MPa;
Thermal Conductivity: 0.050W/M.K;
The Max Temp: 1050c;
Link Shrinkage: 1.5%@1050*3hrs;
Bending Strength: 0.45MPa;
|
Feature: Good Acid Resistance, Good Mechanical Strength, High Refractoriness, Low Thermal Conductivity, Thermal Shock Resistance, Volume Stability;
Production Process: Semi-Dry Pressing;
Refractoriness (℃): 1580< Refractoriness< 1770, 1770< Refractoriness< 2000;
Shape: Brick, Brick;
Type: Silica Brick, Refractory Material;
Material: Silicon Carbide (Sic);
Sio2: 96%;
Fe2o3: 1.0%;
Ap: 22%;
True Density(g/cm3): 2.34;
CCS: 30MPa;
Rul: 1660c;
|
Refractoriness (℃): 1580< Refractoriness< 1770;
Feature: Long Time Materials;
Type: Heat-Resistant Material;
Shape: Plate;
Product Name: Ceramic Fiberglass Mesh Filter;
Temperature: 1450;
Hole Size: 1.5*1.5 2.0*2.0 2.5*2.5;
Mesh Size: 1.5*1.5/2.0*2.0/2.5*2.5/0.8*0.8/1.0*1.0;
Tensile Strenght: 16/8/6;
Operating Temperature: 700~1620celsius;
Melting Point: 900-1700;
Continuous Working Time: 5-10minutes;
Thickness(mm): 0.5/1.5;
Weight(G/M2): 160/190/180/580/550/520;
Color: Brown/Black;
|