| Specification |
Usage: Planting Material, Denture Processing;
Usage Times: Disposable;
Material: Ceramics;
Applicable Departments: Dental Department;
Nature: Specialized Instrument Equipment;
Name: Kingch Dentrue Material Zirconia Block for Implant;
Certificate: ISO 13485 CE;
Color: Vita 16 Color;
Sample Provided: Available;
Molde No: Ht HS St Stc Stm Ut Utc 3dm 3dp;
MOQ: 1 Piece;
Thickness: 10-25mm;
OEM: Availble;
|
Usage: Polishing Material, Dental Consumables;
Usage Times: Disposable;
Applicable Departments: Dental;
Certificate: CE FDA;
Brand: Umg;
MOQ: 200 Box;
|
Usage: Polishing Material, Orthodontic Material, Lining Material, Dental Preventive Health Care Materials, Planting Material, Bonding Material, Filling Material, Model Making;
Usage Times: Non-Disposable;
Material: Resin;
Applicable Departments: Dental Department;
Nature: Shared Instrument Equipment;
Viscosity: 250-350cpimpas;
Density: 1.05~1.25g/cm3(@25ºC);
Flexural Modulus: 1500-2100MPa;
Flexural Strength: 40-50MPa;
Tensile Strength: 35-45 MPa;
Elongation at Break: 25-30%;
Bottom Exposure Time: 20-40s;
Normal Exposure Time: 1.5-3s;
Molding Shrinkage: 4.3-5.6%;
|
Usage: Polishing Material, Orthodontic Material, Lining Material, Dental Preventive Health Care Materials, Planting Material, Bonding Material, Filling Material, Model Making;
Usage Times: Non-Disposable;
Material: Resin;
Applicable Departments: Dental Department;
Nature: Shared Instrument Equipment;
Viscosity: 266 Cpormpa S;
Density: 1.05~1.25g/cm3(@25ºC);
Flexural Modulus: 30.3 MPa;
Flexural Strength: 40-50MPa;
Tensile Strength: 28.1 MPa;
Elongation at Break: 14.6%;
Wavelength: 365-405nm;
Shrinkage: 3.72-4.24%;
Surface Hardness: 78 D;
|
Usage: Polishing Material, Orthodontic Material, Lining Material, Dental Preventive Health Care Materials, Planting Material, Bonding Material, Filling Material, Model Making;
Usage Times: Non-Disposable;
Material: Resin;
Applicable Departments: Dental Department;
Nature: Shared Instrument Equipment;
Viscosity: 350 Cps (@25ºC);
Density: 1.05~1.1g/cm3(@25ºC);
Hardness: D86;
Flexural Modulus: 1376 MPa;
Flexural Strength: 87 MPa;
Tensile Modulus: 720 MPa;
Tensile Strength: 37 MPa;
Elongation at Break: 6;
Impact Strength Notched Izod: 18 J/M;
Heat Deflflection Temperature: 78 ºC;
Purity: 100%;
|