Specification |
Material: Ceramics;
Content: >90%;
Usage: Machinery, Grinding Media;
Processing Type: Rolling Type;
Size: Small;
Color: White;
Customized: Non-Customized;
Shape: Round and Cylindrical;
Sample: Availabale;
|
Material: Alumina;
Content: >90%;
Usage: Construction, Machinery, Chemical, Petroleum, Grind, Refractory Material;
Processing Type: Isostatic Pressing Type;
Size: Middle;
Color: White;
Customized: Customized;
MOQ: 100;
Ceramic Mohs Hard: 9;
Use for: Lining of Equipment and Pipe;
|
Material: Alumina;
Content: >90%;
Usage: Construction, Machinery, Chemical, Petroleum, Grind, Refractory Material;
Processing Type: Isostatic Pressing Type;
Size: Middle;
Color: White;
Customized: Customized;
Quality: First Class;
Delivery Time: 15~25 Days as Your Request;
Samples: Free Samples Can Be Provided;
Hardness: Mohs 9;
Trade Terms: EXW /Fob/CFR/CIF;
|
Material: Zirconia;
Content: 57%;
Usage: Construction, Machinery, Chemical, Petroleum, Grind;
Processing Type: Rolling Type;
Size: Middle;
Color: White;
Customized: Customized;
Al2O3(%): >57;
Zro2(%): >5;
Sio2(%): <30;
Hv Hardness(Gpa): >7;
Crushing Strength(N): >250(D:1.5-2mm);
Water Absorption: <0.01;
Bulk Density(g/cm3): >2.80;
Wear Loss Rate(G/Kg.H): <1.5;
Sphericity: >95%;
|
Material: Alumina;
Content: 75% ~ 80%;
Usage: Construction, Machinery, Chemical, Petroleum, Grind;
Processing Type: Rolling Type;
Size: Middle;
Color: White;
Customized: Customized;
Al2O3(%): >75;
Fe2o3(%): <0.4;
Sio2(%): <20;
Mohs Hardness: 8;
Water Absorption: <0.01;
Bulk Density(g/cm3): >3.15;
Wear Loss(G/Kgh): <1.6;
Crushing Strength(3mm): >800n;
Diameter: 0.5-13mm;
Sphericity: >95%;
|