| Specification |
Material: Stainless Steel;
Type: Hexagon Head;
Connection: Common Bolt;
Head Style: Round;
Standard: DIN, ANSI, GB, JIS, BSW, GOST;
Grade: 6.8;
Application: Machinery, Chemical Industry, Environmental, Building;
Finish: Passivation;
Grade Option: A2-70 A4-80;
Material Option: 18-8 SS304 SS316;
Finish Option: Polishing;
|
Material: High Strength Steel;
Type: Hexagon Head With Flange;
Connection: Common Bolt;
Head Style: Hexagonal;
Standard: DIN, ANSI, GB, JIS, BSW, Accept Non-Standard;
Grade: 5/8/9/8.8/10.9/12.9;
Application: Machinery, Chemical Industry, Automotive Industry;
Finish: Dacromet Coating;
Thread: Metric or Inch;
Thread Type: Fine / Coarse /Bsw/Bsf/ Unc/Unf;
8.8 Hardness: HRC 22-32;
8.8 Tensile Strength: Above 800 MPa;
8.8 Yield Strength: Above 640 MPa;
10.9 Hardness: HRC 33-38;
10.9 Tensile Strength: Above 1040 MPa;
10.9 Yield Strength: Above 940 MPa;
12.9 Hardness: HRC 39-45;
12.9 Tensile Strength: Above 1200MPa;
|
Material: High Strength Steel;
Type: Hexagon Head With Flange;
Connection: Common Bolt;
Head Style: Hexagonal;
Standard: DIN, ANSI, GB, JIS, BSW, Accept Non-Standard;
Grade: 5/8/9/8.8/10.9/12.9;
Application: Machinery, Chemical Industry, Automotive Industry;
Finish: Dacromet Coating;
Thread: Metric or Inch;
Thread Type: Fine / Coarse /Bsw/Bsf/ Unc/Unf;
8.8 Hardness: HRC 22-32;
8.8 Tensile Strength: Above 800 MPa;
8.8 Yield Strength: Above 640 MPa;
10.9 Hardness: HRC 33-38;
10.9 Tensile Strength: Above 1040 MPa;
10.9 Yield Strength: Above 940 MPa;
12.9 Hardness: HRC 39-45;
12.9 Tensile Strength: Above 1200MPa;
|
Material: High Strength Steel;
Type: Hexagon Head With Flange;
Connection: Common Bolt;
Head Style: Hexagonal;
Standard: DIN, ANSI, GB, JIS, BSW, Accept Non-Standard;
Grade: 5/8/9/8.8/10.9/12.9;
Application: Machinery, Chemical Industry, Automotive Industry;
Finish: Dacromet Coating;
Thread: Metric or Inch;
Thread Type: Fine / Coarse /Bsw/Bsf/ Unc/Unf;
8.8 Hardness: HRC 22-32;
8.8 Tensile Strength: Above 800 MPa;
8.8 Yield Strength: Above 640 MPa;
10.9 Hardness: HRC 33-38;
10.9 Tensile Strength: Above 1040 MPa;
10.9 Yield Strength: Above 940 MPa;
12.9 Hardness: HRC 39-45;
12.9 Tensile Strength: Above 1200MPa;
|
Material: High Strength Steel;
Type: Hexagon Head With Flange;
Connection: Common Bolt;
Head Style: Hexagonal;
Standard: DIN, ANSI, GB, JIS, BSW, Accept Non-Standard;
Grade: 5/8/9/8.8/10.9/12.9;
Application: Machinery, Chemical Industry, Automotive Industry;
Finish: Dacromet Coating;
Thread: Metric or Inch;
Thread Type: Fine / Coarse /Bsw/Bsf/ Unc/Unf;
8.8 Hardness: HRC 22-32;
8.8 Tensile Strength: Above 800 MPa;
8.8 Yield Strength: Above 640 MPa;
10.9 Hardness: HRC 33-38;
10.9 Tensile Strength: Above 1040 MPa;
10.9 Yield Strength: Above 940 MPa;
12.9 Hardness: HRC 39-45;
12.9 Tensile Strength: Above 1200MPa;
|