Specification |
Application: Refractory, Industrial Ceramic, Rto/Rco & Heat Storage;
Type: Honeycomb Ceramic Thermal Storage Media;
Cell Shape: Circular, Cell Shape Is Customizable;
Cell Number: Cell Number and Size Are Customizable;
Groove: Plate, Single, Double, Cross, Four Footer, Chute;
Material: Zirconia Corundum;
|
Application: Aerospace, Electronics, Medical, Refractory, Industrial;
Flexural Strength: >1000 MPa;
Purity: 95%;
Type: Ceramic Part;
Material: Zirconia;
Density: 5.7-6.0 g/cm3;
Color: White, Yellow, Blue, Black;
Vicker's Hardness: 1100-1200 MPa;
Compressive Strength: 2200-2500 MPa;
Modulus of Elasticity: 205-250 Gpa;
Thermal Conductivity: 2.5-3.0 W/M.K;
|
Application: Aerospace, Electronics, Medical, Refractory, Industrial;
Flexural Strength: >1000 MPa;
Purity: 95%;
Type: Ceramic Part;
Material: Zirconia;
Density: 5.7-6.0 g/cm3;
Color: White, Yellow, Blue, Black;
Vicker's Hardness: 1100-1200 MPa;
Compressive Strength: 2200-2500 MPa;
Modulus of Elasticity: 205-250 Gpa;
Thermal Conductivity: 2.5-3.0 W/M.K;
|
Application: Aerospace, Electronics, Medical, Refractory, Industrial;
Flexural Strength: >1000 MPa;
Purity: 95%;
Type: Ceramic Ring;
Material: Zirconia;
Density: 5.7-6.0 g/cm3;
Color: White, Yellow, Blue, Black;
Vicker's Hardness: 1100-1200 MPa;
Compressive Strength: 2200-2500 MPa;
Modulus of Elasticity: 205-250 Gpa;
Thermal Conductivity: 2.5-3.0 W/M.K;
|
Application: Aerospace, Electronics, Medical, Refractory, Industrial;
Flexural Strength: >1000 MPa;
Purity: 95%;
Type: Ceramic Part;
Material: Zirconia;
Density: 5.7-6.0 g/cm3;
Color: White, Yellow, Blue, Black;
Vicker's Hardness: 1100-1200 MPa;
Compressive Strength: 2200-2500 MPa;
Modulus of Elasticity: 205-250 Gpa;
Thermal Conductivity: 2.5-3.0 W/M.K;
|