Specification |
CAS No.: 1592-23-0;
Molecular Principal Chain: Carbon Chain Polymer;
Color: White;
Fineness: 90%;
Volatiles: 6.0;
|
CAS No.: 9009-54-5;
Formula: C3h8n2o;
Color: White;
Form: Oval Particles;
Hardness,Shore a: 75-82;
Density,g/cm3: 1.19-1.22;
100% Modulus,MPa: 5-35;
300% Modulus,MPa: 12-43;
Tensile Strength,MPa: 35-60;
Tear Strength,MPa: 100-240;
Procesing Temperature,°c: 165-180;
|
CAS No.: 9009-54-5;
EINECS: 210-898-8;
Molecular Principal Chain: Urethane Based Polymer;
Color: White;
Form: Oval Particles;
Hardness,Shore a: 55-95;
Density,g/cm3: 1.10-1.17;
100% Modulus,MPa: 5-22;
300% Modulus,MPa: 9-30;
Tensile Strength,MPa: 20-42;
Tear Strength,MPa: 75-180;
Elongation at Break,%: 350-700;
Tear Strength,Kn/M: 75-180;
|
Molecular Principal Chain: Urethane Based Polymer;
Color: White;
Form: Oval Particles;
Hardness,Shore a: 55-95;
Density,g/cm3: 1.10-1.17;
100% Modulus,MPa: 5-22;
300% Modulus,MPa: 9-30;
Tensile Strength,MPa: 20-42;
Tear Strength,MPa: 75-180;
Elongation at Break,%: 350-700;
Tear Strength,Kn/M: 75-180;
|
CAS No.: 9009-54-5;
EINECS: 210-898-8;
Molecular Principal Chain: Urethane Based Polymer;
Color: White;
Form: Oval Particles;
Hardness,Shore a: 55-95;
Density,g/cm3: 1.10-1.17;
100% Modulus,MPa: 5-22;
300% Modulus,MPa: 9-30;
Tensile Strength,MPa: 20-42;
Tear Strength,MPa: 75-180;
Elongation at Break,%: 350-700;
Tear Strength,Kn/M: 75-180;
|