Specification |
Usage: High Temperature Insulating Material, Thermal Insulation Material;
Temprature Classification: 1600℃, 1500℃, 1650;
Chemical Composition:: SiO2, Al2O3.SiO2, Al2O3;
Shape: Ceramic Fiber Blanket;
Kind: Alumina Fiber;
Manufacturer: Luyang;
|
Usage: Thermal Insulation Coatings, High Temperature Insulating Material;
Temprature Classification: 1050℃, 650;
Chemical Composition:: Al2O3.SiO2, Al2O3;
Shape: Ceramic Fiber Textile;
Manufacturing Technique: Spray Silk Rug;
Kind: Ordinary Ceramic Fiber;
Working Temperature: 650 1050;
Reinforced: E Glass Filament//Stainless Steel Wire;
Diameter(mm): 3~50;
|
Usage: High Temperature Insulating Material;
Temprature Classification: 1050~1600 C.Degree;
Chemical Composition:: Al2O3+Sio2≥99%;
Shape: Ceramic Fiber Blanket;
Manufacturing Technique: Ceramic Fiber Bulk Wool;
Kind: Ordinary Ceramic Fiber;
Thickness: 6mm-50mm, 1", 1/2"2";
Ultimate Strength (≥ MPa): 0.5MPa (25mm Thickness);
Fiber Diameter: 3-5μm;
Thermal Conductivity: 0.06-0.12;
Classification Temperature: 1200;
Ttensile Strenghth(_Kpa): 30/50/70;
Width: 100mm-1220mm;
Shrinkage (1800 ºF, 3h): 1050~1600 C.Degree;
Density (Kg/M³ ): 128;
Al2O3: ≥43;
Zro2: ≥54;
Permanent Linear Shrinkage: 1000c*24HS2.5;
Density: 64/96/128;
|
Usage: High Temperature Insulating Material;
Temprature Classification: 1600℃, 1500℃, 1400℃, 1260℃, 1050℃;
Chemical Composition:: SiO2, Al2O3.SiO2, Al2O3;
Shape: Ceramic Fiber Plate;
Manufacturing Technique: Vacuum Forming;
Kind: Refractory Material;
|
Usage: High Temperature Insulating Material;
Temprature Classification: 1600℃, 1500℃, 1400℃, 1260℃, 1050℃;
Chemical Composition:: SiO2, Al2O3.SiO2, Al2O3;
Shape: Ceramic Fiber Plate;
Manufacturing Technique: Vacuum Forming;
Kind: Refractory Material;
|