Specification |
Usage: Iron Voltage Electric Material, Thermal Insulation Coatings, Friction Material, Packing Material, Filter Material, High Temperature Insulating Material;
Temprature Classification: 1600℃, 1500℃, 1400℃, 1260℃, 1050℃;
Chemical Composition:: SiO2, Al2O3.SiO2, Al2O3;
Shape: Ceramic Fiber Plate;
Manufacturing Technique: Vacuum Formed;
Kind: High Purity Ceramic Fiber;
|
Usage: High Temperature Insulating Material;
Temprature Classification: 1050℃;
Chemical Composition:: Al2O3.SiO2;
Shape: Ceramic Fiber Plate;
Manufacturing Technique: Spray Silk Rug;
Kind: High Purity Ceramic Fiber;
Size: Customizable;
Certifiacte: ISO9001, CE, etc;
Bulk Density: 320kg/M3;
Specific Heat Capacity(: 0.8kj/Kg.K;
Compressive Strength: 0.3MPa;
Linear Shrinkage(800ºC): 2.0%;
|
Usage: High Temperature Insulating Material;
Temprature Classification: 1050℃;
Chemical Composition:: Al2O3.SiO2;
Shape: Ceramic Fiber Plate;
Manufacturing Technique: Spray Silk Rug;
Kind: High Purity Ceramic Fiber;
Size: Customizable;
Certifiacte: ISO9001, CE, etc;
Bulk Density: 320kg/M3;
Specific Heat Capacity(: 0.8kj/Kg.K;
Compressive Strength: 0.3MPa;
Linear Shrinkage(800ºC): 2.0%;
|
Usage: High Temperature Insulating Material;
Temprature Classification: 1050℃;
Chemical Composition:: Al2O3.SiO2;
Shape: Ceramic Fiber Plate;
Manufacturing Technique: Spray Silk Rug;
Kind: High Purity Ceramic Fiber;
Size: Customizable;
Certifiacte: ISO9001, CE, etc;
Bulk Density: 320kg/M3;
Specific Heat Capacity(: 0.8kj/Kg.K;
Compressive Strength: 0.3MPa;
Linear Shrinkage(800ºC): 2.0%;
|
Usage: Filter Material, High Temperature Insulating Material;
Temprature Classification: 1260℃;
Chemical Composition:: SiO2, Al2O3.SiO2, Al2O3;
Shape: Ceramic Fiber Cotton;
Manufacturing Technique: Spray Silk Rug;
Kind: High Purity Ceramic Fiber;
Density (Kg/M³ ): 160;
Thermal Conductivity: 0.09(400c);
Fiber Diameter: 3-5 Um;
Ultimate Strength (≥ MPa): 0.3;
|