Specification |
Usage: High Temperature Insulating Material;
Temprature Classification: 1600℃, 1500℃, 1400℃, 1260℃, 1050℃;
Chemical Composition:: SiO2, Al2O3.SiO2, Al2O3;
Shape: Ceramic Fiber Plate;
Manufacturing Technique: Ceramic Fiber Board;
Kind: Ordinary Ceramic Fiber;
Province: Shandong;
Name: Ceramic Fiber Board;
Application: Thermal Insulation;
Manufacturer: Luyang;
|
Usage: High Temperature Insulating Material;
Temprature Classification: 1050℃;
Chemical Composition:: Sio2+Cao;
Shape: Board;
Manufacturing Technique: Stirring, Heating, Gelling, Forming, Drying;
Kind: Reinforcing Fiber;
Size: Customizable;
Certifiacte: ISO9001, CE, etc;
Working Temp: 1000c;
Bulk Density: 250kg/M3;
Compressive Strength: 0.52MPa;
Thermal Conductivity: 0.050W/M.K;
The Max Temp: 1050c;
Link Shrinkage: 1.5%@1050*3hrs;
Bending Strength: 0.45MPa;
|
Usage: High Temperature Insulating Material;
Temprature Classification: 1050℃;
Chemical Composition:: Sio2+Cao;
Shape: Board;
Manufacturing Technique: Stirring, Heating, Gelling, Forming, Drying;
Kind: Reinforcing Fiber;
Size: Customizable;
Certifiacte: ISO9001, CE, etc;
Working Temp: 1000c;
Bulk Density: 250kg/M3;
Compressive Strength: 0.52MPa;
Thermal Conductivity: 0.050W/M.K;
The Max Temp: 1050c;
Link Shrinkage: 1.5%@1050*3hrs;
Bending Strength: 0.45MPa;
|
Usage: Thermal Insulation Coatings, Packing Material, Filter Material;
Temprature Classification: 1260℃;
Chemical Composition:: BN, SiO2, B4C, SiC, Al2O3.SiO2, Al2O3;
Shape: Ceramic Fiber Paper;
Manufacturing Technique: Jilt Silk Rug;
Kind: Ordinary Ceramic Fiber;
Product Name: Expanded Graphite Ceramic Fiber Paper;
Density: 220-250 Kg/M3;
Expansion Rate: 500-600 %;
Function: Heat Preservation, Insulation, Sealing;
|
Usage: High Temperature Insulating Material;
Temprature Classification: 1600℃, 1500℃, 1400℃, 1260℃, 1050℃;
Chemical Composition:: Al2O3.SiO2;
Shape: Different Shapes;
Manufacturing Technique: Vacuum Formed;
Kind: High Purity Ceramic Fiber;
Shapes: Can Be Made Different Shapes;
Density: 280kg/M3-450kg/M3;
Color: White;
Organic Type: with Smell;
Inorganic Type: Without Smell;
Application: Boiler, Furnace, Stove etc;
Loss of Ignition, Loi, %: <8;
Permanent Linear Shrinkage, %, 24 Hours: <3;
Compressive Strength: >0.2;
Thermal Conductivity, W/M•K: 0.06-0.18;
|