Specification |
Application: Electronics, Industrial, Steel-Making;
Standard: GB, ASTM;
Purity: 99.91%,99.8%;
Alloy: Non-alloy;
Type: Molybdenum Bar;
Powder: Not Powder;
Density: 9.6g/cm3;
Surface: Sintering Clean Surface;
Working Temperature: 1100-1800;
Property: High Temperature Resistance, Corrision Resistant;
Processing Technique: Sintering Surface;
National Basing: GB/T3462-2017;
Usage: Steel Making Addictive;
Related Products: Molybdenum Wire, Sheet/Plate, Crucible, Boat;
MOQ: 1kg;
Lead Time: Depend on Quantity(7-25days);
Transport Mode: Express, by Air or by Sea;
OEM: Acceptable;
Sample: Available;
Our Advantage: High Quality After-Sale Service;
|
Application: Aviation, Electronics, Industrial, Medical, Chemical;
Standard: JIS, GB, DIN, BS, ASTM, AISI;
Purity: >99.95%;
Alloy: Non-alloy;
Type: Molybdenum Pipe;
Powder: Not Powder;
MOQ: 1kg;
Delivery Time: with 15 Days After Received Payment;
Commodity: Molybdenum Crucible;
Material: Mo-1;
Density: ≥10.2g/ Cm3;
Hv: ≥150;
The Highest Temperature: 1100°c to 1700°c;
|
Application: Electronics, Industrial;
Standard: GB, ASTM;
Purity: >99.95%;
Alloy: Non-alloy;
Type: Molybdenum Boats;
Powder: Not Powder;
Products Name: Tzm Boat in MIM;
Density: 10.2g/cm3;
Wall Thickness: 0.4-10mm;
Width: 20-500mm;
Length: 20-1000mm;
Surface: Hot Rolled, Bright;
Usuage: Sintering and Heat Treatment Furnace;
|
Application: Electronics, Industrial;
Standard: GB, ASTM;
Purity: >99.95%;
Alloy: Non-alloy;
Type: Molybdenum Boats;
Powder: Not Powder;
Products Name: Tzm Charge Carrier Boat;
Density: 10.2g/cm3;
Wall Thickness: 0.4-10mm;
Width: 20-500mm;
Length: 20-1000mm;
Surface: Hot Rolled, Bright;
Usuage: Sintering and Heat Treatment Furnace;
|
Application: Electronics, Industrial;
Standard: GB, ASTM;
Purity: >99.95%;
Alloy: Non-alloy;
Type: Molybdenum Boats;
Powder: Not Powder;
Products Name: Tzm Molybdenum Tray Usedin Annealing Furnace;
Density: 10.2g/cm3;
Wall Thickness: 0.4-10mm;
Width: 20-500mm;
Length: 20-1000mm;
Surface: Hot Rolled, Bright;
Usuage: Sintering and Heat Treatment Furnace;
|