| Specification |
Type: Tungsten Bead;
W Purity: W97%;
Density: 18.5g/cm3;
Size: Dia2.0mm,Dia2.5mm,Dia2.9mm,Dia3.5mm,Dia4.0mm,;
|
Application: Aviation, Electronics, Industrial, Medical, Chemical;
Standard: JIS, GB, DIN, BS, ASTM, AISI;
Purity: >99.95%;
Alloy: Non-alloy;
Shape: Round;
Type: Tungsten Bars;
MOQ: 1kg;
Delivery Time: with 15 Days After Received Payment;
Surface: Black&Polished;
|
Application: Aviation, Electronics, Industrial, Medical, Chemical, Defense;
Standard: ASTM;
Purity: 90%~97%;
Alloy: Alloy;
Shape: Various Shapes;
Type: Short Rod, Round Bar, Cycliner;
Grade: ASTM B777, Class 1, 2, 3 and 4 Wnife/Wnicu;
|
Application: Aviation, Electronics, Industrial, Medical, Chemical, Optical Industry;
Standard: ASTM;
Purity: 90%~97%;
Alloy: Alloy;
Shape: Standard or Customized;
Type: Tungsten Bars;
Supply State: Sintered, Forged and Vacuum Treatment;
Customized: Sheet/Plate/Foil/Strip According to Drawi;
Material: 90%-97%Wnife or 90%-97%Wnicu;
Grade: ASTM B777-15, AMS 7725, AMS-T-21014;
Density G/Cc: 16.85~17.30, 17.15~17.85, 17.75~18.35, 18.25~18.85;
Ultimate Tensile Strength: 758MPa, 724MPa, 689MPa;
Class: 1, 2, 3, 4;
Yield Strength: 517MPa;
Elongation: 5%, 3%, 2%;
Nonmagnetic: Ultimate Strength 648MPa, 648MPa, Na;
Heat Treatment: Sintering;
Other Quanlity: AMS-T-21014, Mil-T-21014;
Dimension: Customized or as Per Drawings;
|
Application: Aviation, Industrial, Defense;
Standard: ASTM, AMS-T-21014;
Purity: 90%~97%;
Alloy: Alloy;
Shape: Round;
Type: Sphere;
Supply State: Sintered (with Band); Grind (Without Band);
Grade: ASTM B777, AMS-T-21014;
Class: 1, 2, 3, 4;
Density: 16.85~17.25, 17.15~17.85, 17.75~18.35, 18.25~18.85;
Tungsten Content %: 90, 92.5, 95, 97;
Hardness: 32HRC, 33HRC, 34HRC, 35HRC;
Tensile Strength: 758MPa, 724MPa, 689MPa;
Yield Strength: 517MPa;
Elongation: 5%, 3%, 2%;
Wolfram: Tungsten Bearing Ball;
Tungsen Alloy: Ball;
Tungsten: Grinding Ball;
Tungsten Alloy Ball: Sintered Ball with Band;
|