Specification |
Refractoriness (℃): 1580< Refractoriness< 1770;
Feature: Long Time Materials;
Type: Refractory Material;
Shape: Brick;
Material: Magnesia-Hecynite;
Application Area: Sintering Zone in Rotary Kiln;
Size: Customer Made;
Bulk Density: 2.9-2.95g/cm3;
Apparent Porosity: 17%;
Tsr 950ºC: 100 Cycle;
Rul: 1650-1700ºC;
CCS MPa: 60;
|
Refractoriness (℃): 1580< Refractoriness< 1770;
Feature: Long Time Materials;
Type: Refractory Material;
Shape: Square, Circular, Triangular, etc;
Material: Mullite, Cordierite, High Alumina, etc;
Size: 50*50, 40*40, 65*65, 50*75, etc;
Hole Shape: Square, Circular, Triangular, Hexagonal, etc;
Holes: 100cpsi, 200cpsi, 300cpsi, etc;
Application: Metallic Molten;
|
Refractoriness (℃): Refractoriness> 2000;
Feature: Long Time Materials;
Type: Heat-Resistant Material;
Shape: Sagger;
Material: Mullite Corundum;
Capacity: 100-200ml;
Color: White;
Looks: Square,Rectangular,Round;
Finsh: Bore, Slot;
Application: Thermal Analysis or Firing;
|
Refractoriness (℃): Refractoriness> 2000;
Feature: Long Time Materials;
Type: Heat-Resistant Material;
Shape: Crucible;
Material: Alumina;
Capacity: 10ml, 20ml, 30ml, 50ml, 80ml, 100ml, 200ml, 500ml;
Color: White;
Finsh: Bore, Slot;
Application: Thermal Analysis or Firing;
Advantage: High Pressure Resistance;
Al2O3 Content (%): 80-90;
|
Refractoriness (℃): 1580< Refractoriness< 1770;
Feature: Long Time Materials;
Type: Refractory Material;
Shape: Pipe;
Material: Silicon Carbide (SiC);
Usage: Widely;
Quality: Better;
Service: Super;
Price: Lower;
|