| Specification |
Application Area: Preheating Zone in Rotary Kiln;
Size: Customer Made;
Bulk Density: 2.9-3.0g/cm3;
Apparent Porosity: 16%;
Tsr 950℃: 100 Cycle;
Rul: 1700℃;
CCS MPa: 60;
MGO: 85-87;
Refractoriness (℃): 1580< Refractoriness< 1770;
Feature: Long Time Materials;
Type: Refractory Material;
Shape: Brick;
Material: Magnesia-Hecynite;
|
Application: Cement Industry, Chemical Industry, Coking Industry, Glass Industry, Steelmaking Industry, Industrial Furnace;
Content: 98% Magnesia Brick;
Performance: High-Purity Magnesia Firebrick;
Production Process: Sintered Magnesia Brick;
Softening Temperature: ≥1650℃;
Keyword: Magnesia Block Refractory Bricks;
Size of Basic Refractory: 230*114*65mm or Special S;
Refractoriness: Super-Class (Refractoriness> 2000;
Apparent Porosity: Max 16%;
Applications: Iron Steel Furnace, Glass Furnace, Ceme;
Refractory Brick Feature: High Refractoriness;
Cold Crushing Strength: Min 60 MPa;
Reheating Linear Change(1650 °c,2h): 0~-0.4;
Advantage: Resist Basic (Alkaline) Slag;
Refractoriness (℃): 1580< Refractoriness< 1770;
Feature: Long Time Materials, High Temperature Resistance, Instant Materials;
Type: Refractory Material;
Shape: Brick;
Material: Magsite;
|
Application: Cement Industry, Chemical Industry, Coking Industry, Glass Industry, Steelmaking Industry, High Temperature Kiln;
Content: 98% Magnesia Brick;
Performance: High-Purity Magnesia Firebrick;
Production Process: Sintered Magnesia Brick;
Softening Temperature: ≥1650℃;
Keyword: Magnesia Block Refractory Bricks;
Size of Basic Refractory: 230*114*65mm or Special S;
Refractoriness: Super-Class (Refractoriness> 2000;
Apparent Porosity: Max 16%;
Applications: Iron Steel Furnace, Glass Furnace, Ceme;
Refractory Brick Feature: High Refractoriness;
Cold Crushing Strength: Min 60 MPa;
Reheating Linear Change(1650 °c,2h): 0~-0.4;
Advantage: Resist Basic (Alkaline) Slag;
Refractoriness (℃): 1580< Refractoriness< 1770;
Feature: Long Time Materials, High Temperature Resistance, Instant Materials;
Type: Refractory Material;
Shape: Brick;
Material: Magsite;
|
Application: Cement Industry, Chemical Industry, Coking Industry, Glass Industry, Steelmaking Industry, High Temperature Kiln;
Content: 98% Magnesia Brick;
Performance: High-Purity Magnesia Firebrick;
Production Process: Sintered Magnesia Brick;
Softening Temperature: ≥1650℃;
Keyword: Magnesia Block Refractory Bricks;
Size of Basic Refractory: 230*114*65mm or Special S;
Refractoriness: Super-Class (Refractoriness> 2000;
Apparent Porosity: Max 16%;
Applications: Iron Steel Furnace, Glass Furnace, Ceme;
Refractory Brick Feature: High Refractoriness;
Cold Crushing Strength: Min 60 MPa;
Reheating Linear Change(1650 °c,2h): 0~-0.4;
Advantage: Resist Basic (Alkaline) Slag;
Refractoriness (℃): 1580< Refractoriness< 1770;
Feature: Long Time Materials, High Temperature Resistance, Instant Materials;
Type: Refractory Material;
Shape: Brick;
Material: Magsite;
|
Application: Cement Industry, Chemical Industry, Coking Industry, Glass Industry, Steelmaking Industry, High Temperature Kiln;
Content: 98% Magnesia Brick;
Performance: High-Purity Magnesia Firebrick;
Production Process: Sintered Magnesia Brick;
Softening Temperature: ≥1650℃;
Keyword: Magnesia Block Refractory Bricks;
Size of Basic Refractory: 230*114*65mm or Special S;
Refractoriness: Super-Class (Refractoriness> 2000;
Apparent Porosity: Max 16%;
Applications: Iron Steel Furnace, Glass Furnace, Ceme;
Refractory Brick Feature: High Refractoriness;
Cold Crushing Strength: Min 60 MPa;
Reheating Linear Change(1650 °c,2h): 0~-0.4;
Advantage: Resist Basic (Alkaline) Slag;
Refractoriness (℃): 1580< Refractoriness< 1770;
Feature: Long Time Materials, High Temperature Resistance, Instant Materials;
Type: Refractory Material;
Shape: Brick;
Material: Magsite;
|