Specification |
Refractoriness (℃): 1580< Refractoriness< 1770;
Feature: Long Time Materials;
Type: Refractory Material;
Shape: Brick;
Material: Magnesia-Hecynite;
Application Area: Sintering Zone in Rotary Kiln;
Size: Customer Made;
Bulk Density: 2.9-3.0g/cm3;
Apparent Porosity: 17;
Tsr 950ºC: 100 Cycle;
Rul: 1650-1700ºC;
CCS MPa: 60;
|
Refractoriness (℃): Refractoriness> 2000;
Feature: Long Time Materials;
Type: Refractory Material;
Shape: Block;
Material: Alumina Block;
Chemical Al2O3: Min: 95%;
Advantage: Manufacturer, Can Be Customized;
|
Classification: Clay, Clay;
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Low Thermal Conductivity, Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Low Thermal Conductivity, Long Time Materials;
Production Process: Extrusion Method, Extrusion Method;
Refractoriness (℃): 1580< Refractoriness< 1770, 1580< Refractoriness< 1770;
Shape: Brick, Brick;
Type: Refractory Material;
Material: Alumina Block;
Al2O3: 35%~45%;
Size: Customizable;
Certifiacte: ISO9001, CE, etc;
Refractoriness: Sk32-34;
Apparent Porosity: 13-26%;
Bulk Density: 2.25-2.65g/cm3;
Refractoriness Under [email protected]: 1250-1500;
Thermal Linear Expansion@1000deg: 0.6%;
Fe2o3: 1.8-3.0%;
|
Refractoriness (℃): 1580< Refractoriness< 1770;
Feature: Long Time Materials;
Type: Refractory Material;
Shape: Plate;
Material: Alumina Cement;
Product Name: Alumina Ceramic Foam Filter;
Pore Size: 10-60ppi;
Thickness: 11-50mm;
Dimension Size: 35-500mm;
|
Refractoriness (℃): 1200-1700;
Feature: Long Time Materials;
Type: Refractory Material;
Shape: Bowl;
Material: Aluminium Silicate Material;
Name: Ceramic Fiber Sample Spoon;
Standard: 150 Ml;
Spoon Handle Material: Q235 Steel;
Chemical Composition: Al2O3+Sio2≥98%;
|