Specification |
Refractoriness (℃): 1770< Refractoriness< 2000;
Feature: Long Time Materials;
Type: Refractory Material;
Shape: Plate;
Material: Alumina Cement;
Color: Ivory White;
Purity: 95%--99.7%;
Density: 3.6 - 3.9g / Cm3;
Woeking Temperature: 1500c-1800c;
Thickness: 0.5mm to 50mm;
Tolerance: +/-0.02mm;
Surface Roughness: Ra0.2um;
Delivery Time: 6-30days;
Product Name: Alumina Ceramic Plate;
|
Refractoriness (℃): Refractoriness> 2000;
Feature: Long Time Materials;
Type: Refractory Material;
Shape: Grit / Powder/ Grain;
Material: Brown Fused Alumina;
Grit 1: 0-1mm, 1-3mm, 3-5mm, 5-8mm, 8-15mm;
Grit 2: 0-200 Mesh, 0-325 Mesh;
Chemical Al2O3: Min: 95%, Typical Value 95.3%;
Application: Wear-Resistant and Refractory Products;
More Applications: Reusable Abrasive, Resin Bond Abrasive Tools;
Advantage: Manufacturer;
Other Name: Brown Corundum;
|
Refractoriness (℃): 800 to 1700;
Feature: Long Time Materials;
Type: Refractory Material;
Shape: Blanket;
Material: Alumina Block;
|
Refractoriness (℃): Refractoriness> 2000;
Feature: Long Time Materials;
Type: Refractory Material;
Shape: Block;
Material: Alumina Block;
Advantage: Manufacturer, Can Be Customized;
Al2O3: 95% Min;
Fe2o3: 0.3% Max;
Sio2: 1.2% Max;
TiO2: 3.0% Max;
Cao: 0.4%;
MGO: 0.4%;
Magnetic Particles: 0.05% Max;
Hardness: 9 Mohs;
Specific Gravity: 3.8 g/cm3 Min;
Application: Refractory Bricks, Castables, Other Materials;
|
Refractoriness (℃): 1580< Refractoriness< 1770;
Feature: Long Time Materials;
Type: Refractory Material;
Shape: Brick;
Material: MGO;
Size: Customizable;
Certifiacte: ISO9001, CE, etc;
Apparent Porosity: 15-16%;
Bulk Density: 2.9-3.0;
Cold Crushing Strength: 55-80MPa;
Thermal Shock Resistance Air Cool: 10;
MGO: 92-97.5%;
Cao: 1.2-2.5%;
Sio2: 0.6-3.5%;
|