Specification |
Application: Semiconductor, 3D Hot Bending Glass Die;
Carbon Content: High-Carbon;
Density: 1.85 g/cm3;
Sample: Available;
Particle Size: 5~7 Micron;
Grade: Industrial Grade;
Forming Way: Isostatic Graphite;
Crystal Morphology: Compact Crystalline Graphite;
Type: Graphite Block;
Composition: Carbon;
|
Application: Chemical Industry, Metallurgical Industry, General;
Carbon Content: High-Carbon;
Customization: Yes;
Grain Size: 0.8mm;
Size and Shape: Different Sizes;
Chemical Composition: Carbon;
Density: 1.8 g/cm3;
Max.Grain Size: 0.8 mm;
Specific Resistance: 7.5 Ω;
Flexural Strength: 20.5 MPa;
Compressive Strength: 46 MPa;
Cte*(to 100°c): 2.6;
Thermal Conductivity: 160 W/Mk;
Ash: 0.09%;
Grade: Industrial Grade;
Forming Way: Extruded Graphite;
Type: Articifial Graphite;
Composition: Carbon;
Crystal Morphology: Block;
|
Application: General;
Carbon Content: High-Carbon;
Customization: Yes;
Grain Size: 0.8mm;
Size and Shape: Different Sizes;
Chemical Composition: Carbon;
Density: 1.8 g/cm3;
Max.Grain Size: 0.8 mm;
Specific Resistance: 7.5 Ω;
Flexural Strength: 20.5 MPa;
Compressive Strength: 46 MPa;
Cte*(to 100°c): 2.6;
Thermal Conductivity: 160 W/Mk;
Ash: 0.09%;
Grade: Industrial Grade;
Forming Way: Extruded Graphite;
Type: Articifial Graphite;
Composition: Carbon;
Crystal Morphology: Block;
|
Application: General;
Carbon Content: High-Carbon;
Customization: Yes;
Grain Size: 13~15 Um;
Chemical Composition: Carbon;
Density: 1.80 g/cm3;
Er: 8~11 Ω;
Thermal Conductivity( 100°c): 125 W/M.K;
Cte(The Temperature- 600°c): 4.9;
Shore Hardness: 45 Hsd;
Flexural Strength: 40 MPa;
Compressive Strength: 70 MPa;
Porosity: 16%;
Ash: 500 Ppm;
Partical Size: 13~15 Micron;
Grade: Industrial Grade;
Forming Way: Molded Graphite;
Type: Graphite;
Composition: Carbon;
|
Application: Chemical Industry, Electroplating Industry, Metallurgical Industry, EDM, Photovoltaic, Glass;
Carbon Content: High-Carbon;
Customization: Yes;
Grain Size: 8~10 Um;
Chemical Composition: Carbon;
Density: 1.90 g/cm3;
Er: 11~13 μΩm;
Shore Hardness: 70 Hsd;
Flexural Strength: 60 MPa;
Compressive Strength: 135 MPa;
Thermal Conductivity( 100°c): 115 W/M.K;
Cte(The Temperature- 600°c): 5.85;
Porosity: 11%;
Ash: 50 Ppm;
Particle Size: 8~10 Micron;
Grade: Industrial Grade;
Forming Way: Isostatic Graphite;
Type: Graphite;
Composition: Carbon;
|