Specification |
Application: Industrial Ceramic, Alumina Ceramic;
Material: Alumina Ceramic;
Type: Ceramic Plates;
Useful: Aluminium Filtrate;
|
Application: Refractory, Industrial Ceramics;
Grain Size: 1-10um;
Purity: 95%;
Type: Ceramic Part;
Pressing Speed: Punch Forming;
Suppression Method: Unidirectional Pressurization;
Color: Ivory, Cream, White, Pink Color;
Shape: Arc, Conical, Cylinderical, Tubular, Tall Form, Low for;
Advantage: High Temperature and Chemical Corrosion, High Vacuu;
Usage: Sintering and Melting of Glass, Phosphors, Ceramics;
Applicat: for Chemical Calcining, Metal Casting, and Ceramic;
Working Temperature: 1600c, 1700c, 1800c;
|
Application: Refractory, Industrial Ceramic, Foundry Molten Metal Filtration;
Material: Zirconia Ceramic;
Type: Ceramic Plates;
Main Material: Zro2;
Color: Yellow;
Working Temperature: up to 1700 Degree C;
Hole Density: 10/20ppi (Ppi=Pores Per Inch);
Porosity(%): 80-87;
Compressive Strength(MPa): 1.5 (Room Temperature);
Bulk Density(g/cm3): 0.9-1.3;
Thermal Shock Resistance: 3times/1350 Degree C to Room Temperature;
Size: 35-200mm;
|
Application: Refractory, Industrial Ceramic, Foundry Molten Metal Filtration;
Material: Zirconia Ceramic;
Type: Ceramic Plates;
Main Material: Zro2;
Color: Yellow;
Working Temperature: up to 1700 Degree C;
Hole Density: 10/20ppi (Ppi=Pores Per Inch);
Porosity(%): 80-87;
Compressive Strength(MPa): 1.5 (Room Temperature);
Bulk Density(g/cm3): 0.9-1.3;
Thermal Shock Resistance: 3times/1350 Degree C to Room Temperature;
Size: 35-200mm;
|
Application: Refractory, Industrial Ceramics;
Grain Size: 1-10um;
Purity: 95%;
Type: Ceramic Part;
Pressing Speed: Punch Forming;
Suppression Method: Unidirectional Pressurization;
Color: Ivory, Cream, White, Pink Color;
Shape: Arc, Conical, Cylinderical, Tubular, Tall Form, Low for;
Advantage: High Temperature and Chemical Corrosion, High Vacuu;
Usage: Sintering and Melting of Glass, Phosphors, Ceramics;
Applicat: for Chemical Calcining, Metal Casting, and Ceramic;
Working Temperature: 1600c, 1700c, 1800c;
|