| Specification |
Usage: High Temperature Insulating Material;
Temprature Classification: 1400℃, 1260℃, 1050℃;
Shape: Ceramic Fiber Chunking;
Kind: High Purity Ceramic Fiber;
Temperature: 1260c, 1350c, 1430c;
|
Usage: High Temperature Insulating Material, Thermal Insulation Lining;
Temprature Classification: 1050℃, 1050ºC - 1600ºC;
Chemical Composition:: Al2O3.SiO2, Al2O3, Zro2;
Shape: Board, Panel, Block;
Manufacturing Technique: Wet Forming Process;
Kind: High Purity Ceramic Fiber;
Grade: Std 1260;
Color: Pure White;
Density: 280-320 Kg/M3;
Compressive Strength: 0.3 MPa;
Loss of Ignition: ≤6;
Regular Size: 1200 * 1000, 1000 * 600, 900 * 600;
Regular Thicknesses: 3 - 100 mm Available;
Special Size: Can Be Customzied;
Features: Excellent Thermal Shock Resistance, Easy to Cut, H;
Application: Back up Insulations for Brick and Monolithic Refra;
OEM: Yes;
|
Usage: High Temperature Insulating Material, Thermal Insulation Lining;
Temprature Classification: 1050℃, 1050ºC - 1600ºC;
Chemical Composition:: Al2O3.SiO2, Al2O3, Zro2;
Shape: Board, Panel, Block;
Manufacturing Technique: Wet Forming Process;
Kind: High Purity Ceramic Fiber;
Grade: Std 1260;
Color: Pure White;
Density: 280-320 Kg/M3;
Compressive Strength: 0.3 MPa;
Loss of Ignition: ≤6;
Regular Size: 1200 * 1000, 1000 * 600, 900 * 600;
Regular Thicknesses: 3 - 100 mm Available;
Special Size: Can Be Customzied;
Features: Excellent Thermal Shock Resistance, Easy to Cut, H;
Application: Back up Insulations for Brick and Monolithic Refra;
OEM: Yes;
|
Usage: High Temperature Insulating Material, Thermal Insulation Lining;
Temprature Classification: 1050℃, 1050ºC - 1600ºC;
Chemical Composition:: Al2O3.SiO2, Al2O3, Zro2;
Shape: Board, Panel, Block;
Manufacturing Technique: Wet Forming Process;
Kind: High Purity Ceramic Fiber;
Grade: Std 1260;
Color: Pure White;
Density: 280-320 Kg/M3;
Compressive Strength: 0.3 MPa;
Loss of Ignition: ≤6;
Regular Size: 1200 * 1000, 1000 * 600, 900 * 600;
Regular Thicknesses: 3 - 100 mm Available;
Special Size: Can Be Customzied;
Features: Excellent Thermal Shock Resistance, Easy to Cut, H;
Application: Back up Insulations for Brick and Monolithic Refra;
OEM: Yes;
|
Usage: High Temperature Insulating Material, Thermal Insulation Lining;
Temprature Classification: 1050℃, 1050ºC - 1600ºC;
Chemical Composition:: Al2O3.SiO2, Al2O3, Zro2;
Shape: Board, Panel, Block;
Manufacturing Technique: Wet Forming Process;
Kind: High Purity Ceramic Fiber;
Grade: Std 1260;
Color: Pure White;
Density: 280-320 Kg/M3;
Compressive Strength: 0.3 MPa;
Loss of Ignition: ≤6;
Regular Size: 1200 * 1000, 1000 * 600, 900 * 600;
Regular Thicknesses: 3 - 100 mm Available;
Special Size: Can Be Customzied;
Features: Excellent Thermal Shock Resistance, Easy to Cut, H;
Application: Back up Insulations for Brick and Monolithic Refra;
OEM: Yes;
|