Specification |
Usage: High Temperature Insulating Material;
Temprature Classification: 1400℃, 1260℃, 1050℃, 1430 ºC;
Chemical Composition:: Al2O3.SiO2;
Shape: Ceramic Fiber Blanket;
Manufacturing Technique: Double- Needled;
Kind: High Purity Ceramic Fiber;
Item: Ceramic Fiber Blanket;
Temperature: 1050-1430 C;
Density: 64/96/128/160 Kg/M3;
Color: White/ Pure White;
Al203+Sio2: 97-99 %;
Application: Heat Insulation;
Refractory Grade: Non-Inflammable;
Melting Point: 1760 ºC;
Thickness: 6mm-50mm Thickness;
Width: 610mm/1220mm or Customized;
Length: 3600/3660/3810/7200/7620mm or Customized;
Tensile Strength: >30 Kpa;
Type: Heat-Resistant Material;
Thermal Conductivity (W/M·K): 0.035-0.18;
Performance: Excellent;
|
Usage: Friction Material, High Temperature Insulating Material;
Temprature Classification: 1600℃, 1500℃, 1400℃, 1260℃, 1050℃;
Chemical Composition:: Al2O3.SiO2;
Shape: Blanket;
Manufacturing Technique: Spray Silk Rug;
Kind: High Purity Ceramic Fiber;
Product Name: Eramic Fiber Blanket with Foil;
Application: Refractory;
Thickness: 10-50mm;
Width: 610/1220mm;
Length: 3600/7200/14640mm, 7200-3600;
Chemical Composition: Al2O3+Sio2;
Ultimate Strength (≥ MPa): 0.04;
Working Temperature: 1000-1350;
Fiber Diameter: 3-5um;
Shrinkage (1800 ºF, 3h): 3%(24 Hours);
Thermal Conductivity: 0.055-0.180(W.K.M.);
Density (Kg/M³ ): 160;
Color: Pure White;
|
Usage: Friction Material, High Temperature Insulating Material;
Temprature Classification: 1400℃, 1260℃, 1050℃;
Chemical Composition:: Al2O3.SiO2;
Shape: Blanket;
Manufacturing Technique: Spray Silk Rug;
Kind: High Purity Ceramic Fiber;
Product Name: Ceramic Fiber Blanket;
Application: Refractory;
Thickness: 10-50mm;
Width: 610/1220mm;
Length: 3600/7200/14640mm, 7200-3600;
Chemical Composition: Al2O3+Sio2;
Ultimate Strength (≥ MPa): 0.04;
Working Temperature: 1000-1350;
Fiber Diameter: 3-5um;
Shrinkage (1800 ºF, 3h): 3%(24 Hours);
Thermal Conductivity: 0.055-0.180(W.K.M.);
Density (Kg/M³ ): 160;
Color: Pure White;
|
Usage: Friction Material, High Temperature Insulating Material;
Temprature Classification: 1400℃, 1260℃, 1050℃;
Chemical Composition:: Al2O3.SiO2;
Shape: Blanket;
Manufacturing Technique: Spray Silk Rug;
Kind: High Purity Ceramic Fiber;
Product Name: Ceramic Fiber Blanket;
Application: Refractory;
Thickness: 10-50mm;
Width: 610/1220mm;
Length: 3600/7200/14640mm, 7200-3600;
Chemical Composition: Al2O3+Sio2;
Ultimate Strength (≥ MPa): 0.04;
Working Temperature: 1000-1350;
Fiber Diameter: 3-5um;
Shrinkage (1800 ºF, 3h): 3%(24 Hours);
Thermal Conductivity: 0.055-0.180(W.K.M.);
Density (Kg/M³ ): 160;
Color: Pure White;
|
Usage: Friction Material, High Temperature Insulating Material;
Temprature Classification: 1400℃, 1260℃, 1050℃;
Chemical Composition:: Al2O3.SiO2;
Shape: Blanket;
Manufacturing Technique: Spray Silk Rug;
Kind: High Purity Ceramic Fiber;
Product Name: Refractory Insulation Blanket;
Application: Refractory;
Thickness: 10-50mm;
Width: 610/1220mm;
Length: 3600/7200/14640mm, 7200-3600;
Chemical Composition: Al2O3+Sio2;
Ultimate Strength (≥ MPa): 0.04;
Working Temperature: 1000-1350;
Fiber Diameter: 3-5um;
Shrinkage (1800 ºF, 3h): 3%(24 Hours);
Thermal Conductivity: 0.055-0.180(W.K.M.);
Density (Kg/M³ ): 160;
Color: Pure White;
|