Specification |
Refractoriness (℃): 1580< Refractoriness< 1770;
Feature: Long Time Materials, Thermal Insulation;
Type: Heat-Resistant Material;
Shape: Brick;
Material: Mullite;
Al2O3: 40-70%;
Fe2o3: 0.5-2.0%;
Bulk Density: 0.6-1.1 g/cm3;
Product Name: Insulating Brick;
Certifiacte: ISO9001, CE, etc;
Cold Crushing Strength: 1-3 MPa;
Classification Temperature: 1200~1600ºC;
Application: Industrial Furnace;
Performance: Excellent;
Grade: Jm23/Jm26/Jm28/Jm30/Jm32;
Thermal Conductivity: Low;
Color: White;
Size Control: Accurate;
Production Time: 15-30 Days;
Testing Laboratory: Support;
|
Refractoriness (℃): 1770< Refractoriness< 2000;
Feature: Long Time Materials;
Type: Refractory Material;
Shape: Rod;
Material: Alumina Cement;
Color: Ivory;
Working Temperature: 1500c - 1800c;
Tolerance: +/-0.02mm;
Surface Roughness: Ra 0.2um;
Purity: 95%-99.7%;
Size: Customized;
Delivery Time: 6-30days;
Product Name: Alumina Ceramic Rod;
|
Refractoriness (℃): 1770< Refractoriness< 2000;
Feature: Long Time Materials;
Type: Refractory Material;
Shape: Rod;
Material: Alumina Cement;
Color: Ivory White;
Density: 3.6 - 3.9g / Cm3;
Purity: 95%-99.7%;
Working Temperature: 1500c - 1800c;
Size Tolerance: +/-0.02mm;
Surface Roughness: Ra 0.2um;
Delivery Time: 6-30days;
Size: Customized;
Product Name: Alumina Ceramic Rod;
Raw Material: 95-99.7% Alumina Ceramic;
|
Refractoriness (℃): 1260;
Feature: Instant Materials;
Type: Heat-Resistant Material;
Shape: Roll;
Material: Al2O3_Si2o3;
Permanent Rate of Liner(%)(24h): -3;
Density: 96/128kg/M3;
Tensile Strength: 0.04MPa;
Al2O3+Sio2: 97/99;
|
Refractoriness (℃): 1580< Refractoriness< 1770;
Feature: Long Time Materials;
Type: Refractory Material;
Shape: Square, Circular, Triangular, etc;
Material: Mullite, Cordierite, High Alumina, etc;
Size: 50*50, 40*40, 65*65, 50*75, etc;
Hole Shape: Square, Circular, Triangular, Hexagonal, etc;
Holes: 100cpsi, 200cpsi, 300cpsi, etc;
Application: Casting;
|