Specification |
Refractoriness (℃): 1580< Refractoriness< 1770;
Feature: Long Time Materials;
Type: Refractory Material;
Shape: Brick;
Material: Alumina Block;
Al2O3: 35-80%;
Fe2o3: 1.5-3.0%;
Bulk Density: 2.15-2.80 g/cm3;
Apparent Porosity: 16-24;
Certifiacte: ISO9001, CE, etc;
Cold Crushing Strength: 30-100 MPa;
Working Temperature: 1200~1700ºC;
Application: Industrial Furnace;
Thermal Shock Resistance: Excellent;
Refractoriness: Sk32/Sk34/Sk35/Sk36/Sk37/Sk38;
Refractoriness Under Load (0.2MPa): 1350-1700 ºC;
Color: Yellow;
Size Control: Accurate;
Production Time: 15-30 Days;
Testing Laboratory: Support;
|
Refractoriness (℃): 1580< Refractoriness< 1770;
Feature: Long Time Materials, Square or Rectangle;
Type: Heat-Resistant Material;
Shape: Plate;
Material: Alumina;
Alumina Content: 65;
Size: Customed;
Color: White,Grey;
End: Kiln Part;
Application: High Temperature Resistant, High Wear Resistance;
Finish: Collar, Slot, Curve;
|
Refractoriness (℃): 1580< Refractoriness< 1770;
Feature: Long Time Materials, Square or Rectangle;
Type: Heat-Resistant Material;
Material: Alumina;
Alumina Content: 65;
Size: Customed;
Color: White,Grey;
End: Kiln Part;
Application: High Temperature Resistant, High Wear Resistance;
Finish: Collar, Slot, Curve;
|
Refractoriness (℃): 1580< Refractoriness< 1770;
Feature: Long Time Materials;
Type: Refractory Material;
Shape: Plate;
Material: Silicon Carbide (SiC);
Product Name: Ceramic Foam Filter;
|
Refractoriness (℃): 1580< Refractoriness< 1770;
Feature: Long Time Materials;
Type: Heat-Resistant Material;
Shape: Pipe;
Material: 2.4879,1.4852,Zg45ni48cr28W5si2,More1,More2;
Standard: ANSI,ASTM,ASME,DIN,GB;
Surface Roughness: Ra6.3;
Machining Tolerance: +/-0.01mm;
|