Specification |
Feature: Long Time Materials;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Brick;
Al2O3: 40-70%;
Fe2o3: 0.5-2.0%;
Bulk Density: 0.6-1.1 g/cm3;
Product Name: Insulating Brick;
Certifiacte: ISO9001, CE, etc;
Cold Crushing Strength: 1-3 MPa;
Classification Temperature: 1200~1600ºC;
Application: Industrial Furnace;
Performance: Excellent;
Grade: Jm23/Jm26/Jm28/Jm30/Jm32;
Thermal Conductivity: Low;
Color: White;
Size Control: Accurate;
Production Time: 15-30 Days;
Testing Laboratory: Support;
Type: Heat-Resistant Material;
Material: Mullite;
|
Feature: Long Time Materials;
Refractoriness (℃): 1260c, 1360c, 1400c;
Shape: Ceramic Fiber Module;
Type: Heat-Resistant Material;
Material: Al2O3+Sio2;
|
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Light Weight, Low Thermal Conductivity;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Plate, Ceramic Fiber Plate;
Usage: High Temperature Insulating Material;
Temprature Classification: 1050℃;
Chemical Composition: Al2O3.Sio2;
Manufacturing Technique: Spray Silk Rug;
Kind: High Purity Ceramic Fiber;
Size: Customizable;
Certifiacte: ISO9001, CE, etc;
Bulk Density: 320kg/M3;
Specific Heat Capacity(: 0.8kj/Kg.K;
Compressive Strength: 0.3MPa;
Linear Shrinkage(800ºC): 2.0%;
|
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Light Weight, Low Thermal Conductivity;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Plate, Ceramic Fiber Plate;
Usage: High Temperature Insulating Material;
Temprature Classification: 1050℃;
Chemical Composition: Al2O3.Sio2;
Manufacturing Technique: Spray Silk Rug;
Kind: High Purity Ceramic Fiber;
Size: Customizable;
Certifiacte: ISO9001, CE, etc;
Bulk Density: 320kg/M3;
Specific Heat Capacity(: 0.8kj/Kg.K;
Compressive Strength: 0.3MPa;
Linear Shrinkage(800ºC): 2.0%;
|
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Light Weight, Low Thermal Conductivity;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Plate, Ceramic Fiber Plate;
Usage: High Temperature Insulating Material;
Temprature Classification: 1050℃;
Chemical Composition: Al2O3.Sio2;
Manufacturing Technique: Spray Silk Rug;
Kind: High Purity Ceramic Fiber;
Size: Customizable;
Certifiacte: ISO9001, CE, etc;
Bulk Density: 320kg/M3;
Specific Heat Capacity(: 0.8kj/Kg.K;
Compressive Strength: 0.3MPa;
Linear Shrinkage(800ºC): 2.0%;
|