Specification |
Bonding Function: High Temperature Resistant Adhesive;
Morphology: Solid-State;
Application: Automobile, Construction, Woodworking, Footwear & Leather, Fiber & Garment, Packing;
Material: Polyurethane;
Classification: Hot Melt;
Main Agent Composition: Inorganic Adhesive Material;
Characteristic: Weatherability;
Promoter Composition: Curing Agent;
Composition: Inorganic Material;
Color: White;
|
CAS No.: Other;
Formula: Other;
EINECS: Other;
Bonding Function: Structural Adhesive;
Morphology: Ointment;
Application: Automobile, Construction, Woodworking;
Material: Silicone;
Classification: Room Curing;
Main Agent Composition: Natural Polymer;
Characteristic: Waterproof;
Promoter Composition: Curing Agent;
Composition: Organic Material;
Color: White;
|
CAS No.: Other;
Formula: Mixture;
EINECS: Other;
Bonding Function: Structural Adhesive;
Morphology: Paste;
Application: Automobile, Construction, Woodworking;
Material: Silicone;
Classification: Room Curing;
Main Agent Composition: Natural Polymer;
Characteristic: Waterproof;
Promoter Composition: Curing Agent;
Composition: Organic Material;
Color: Clear;
|
CAS No.: N/a;
Formula: N/a;
EINECS: N/a;
Bonding Function: Thermal Paste;
Morphology: Curing Glue;
Application: Automobile, Woodworking;
Material: Silicone;
Classification: Silicone Glue;
Main Agent Composition: Inorganic Adhesive Material;
Characteristic: Aging Resistance;
Promoter Composition: Curing Agent;
Composition: Inorganic Material;
Color: Gray;
Viscosity (After Mixing)@25 Degrees: 2000cps;
Opening Hours @25 Degrees: More Than 60min;
Curing Conditions: 30min/80 Degrees;
Thermal Conductivity: 0.48;
Thermal Resistance: 0.0043;
Hardness: 47 Shore a;
Density: 1.5 g/cm3;
Tensile Strength: More Than 0.5 MPa;
Elongation at Break: More Than 10%;
Flammability Rating: V-0;
Breakdown Strength: More Than 15 Kv/mm;
|
CAS No.: N/a;
Formula: N/a;
EINECS: N/a;
Bonding Function: Thermal Paste;
Morphology: Curing Glue;
Application: Automobile, Woodworking;
Material: Silicone;
Classification: Silicone Glue;
Main Agent Composition: Inorganic Adhesive Material;
Characteristic: Aging Resistance;
Promoter Composition: Curing Agent;
Composition: Inorganic Material;
Color: Gray;
Viscosity (After Mixing)@25 Degrees: 2000cps;
Opening Hours @25 Degrees: More Than 60min;
Curing Conditions: 30min/80 Degrees;
Thermal Conductivity: 0.48;
Thermal Resistance: 0.0043;
Hardness: 47 Shore a;
Density: 1.5 g/cm3;
Tensile Strength: More Than 0.5 MPa;
Elongation at Break: More Than 10%;
Flammability Rating: V-0;
Breakdown Strength: More Than 15 Kv/mm;
|