| Specification |
Refractoriness (℃): 1580< Refractoriness< 1770;
Feature: Long Time Materials, Long Time Materials, Instant Materials;
Type: Refractory Material, Ceramic Crucible;
Shape: Crucible, Conical, Circular, Cylindrical;
Material: Alumina Cement, Clay, Clay;
Refractoriness: 1580< Refractoriness< 1770;
Color: White, Light Yellow;
Name: Fire Assay Crucible for Lab Muffle Furnace;
Max. Working Temperature: 1650 Degree Celsius;
Item: Ceramic Crucible;
Application: Thermal Analysis or Firing;
Capacity: 10ml, 20ml, 30ml, 50ml, 80ml, 100ml, 200ml, 500ml;
Purpose: Gold Smelting and Assaying;
Size: 30g, 40g, 45g, 50g, 65g;
Usage: Melting, Assaying;
Refractoriness Under Load: 1420 Degree Celsius;
Packing: Wooden Packing, Paper Carton Packing;
|
Refractoriness (℃): 1770< Refractoriness< 2000;
Feature: Long Time Materials, Instant Materials, High Temperature Resistance;
Type: Refractory Material;
Shape: Brick;
Material: MgO-Carbon Brick;
Product Name: Magnesite Carbon Fire Brick;
Bulk Density/ g/cm3: More Than 2.77;
Brick Feature: Great Performance to Anti-Slag;
Cold Crushing Strength(MPa): More Than 25 MPa;
Size: 230mm*114mm*65/75mm or Other Sizes;
Apparant Porosity: Less Than 6;
Modulus of Rupture: More Than 4 MPa;
MGO Content (%): 72%-84%, More Than 70%;
Cao Content (%): 8%-14%;
|
Refractoriness (℃): 1770< Refractoriness< 2000;
Feature: Long Time Materials, Instant Materials, High Temperature Resistance;
Type: Refractory Material;
Shape: Brick;
Material: MgO-Carbon Brick;
Product Name: Magnesite Carbon Fire Brick;
Bulk Density/ g/cm3: More Than 2.77;
Brick Feature: Great Performance to Anti-Slag;
Cold Crushing Strength(MPa): More Than 25 MPa;
Size: 230mm*114mm*65/75mm or Other Sizes;
Apparant Porosity: Less Than 6;
Modulus of Rupture: More Than 4 MPa;
MGO Content (%): 72%-84%, More Than 70%;
Cao Content (%): 8%-14%;
|
Refractoriness (℃): 1770< Refractoriness< 2000;
Feature: Long Time Materials, Instant Materials, High Temperature Resistance;
Type: Refractory Material;
Shape: Brick;
Material: MgO-Carbon Brick;
Product Name: Magnesite Carbon Fire Brick;
Bulk Density/ g/cm3: More Than 2.77;
Brick Feature: Great Performance to Anti-Slag;
Cold Crushing Strength(MPa): More Than 25 MPa;
Size: 230mm*114mm*65/75mm or Other Sizes;
Apparant Porosity: Less Than 6;
Modulus of Rupture: More Than 4 MPa;
MGO Content (%): 72%-84%, More Than 70%;
Cao Content (%): 8%-14%;
|
Refractoriness (℃): 1770< Refractoriness< 2000;
Feature: Long Time Materials, Instant Materials, High Temperature Resistance;
Type: Refractory Material;
Shape: Brick;
Material: MgO-Carbon Brick;
Product Name: Magnesite Carbon Fire Brick;
Bulk Density/ g/cm3: More Than 2.77;
Brick Feature: Great Performance to Anti-Slag;
Cold Crushing Strength(MPa): More Than 25 MPa;
Size: 230mm*114mm*65/75mm or Other Sizes;
Apparant Porosity: Less Than 6;
Modulus of Rupture: More Than 4 MPa;
MGO Content (%): 72%-84%, More Than 70%;
Cao Content (%): 8%-14%;
|