Specification |
Refractoriness (℃): 1580< Refractoriness< 1770;
Feature: Long Time Materials, Long Time Materials, Instant Materials;
Type: Refractory Material, Ceramic Crucible;
Shape: Crucible, Conical, Circular, Cylindrical;
Material: Alumina Cement, Clay;
Refractoriness: 1580< Refractoriness< 1770;
Color: White, Light Yellow;
Name: Clay Pot Crucible Fire Assay Crucible;
Max. Working Temperature: 1650 Degree Celsius;
Item: Ceramic Crucible;
Application: Thermal Analysis or Firing;
Capacity: 10ml, 20ml, 30ml, 50ml, 80ml, 100ml, 200ml, 500ml;
Purpose: Gold Smelting and Assaying;
Size: 30g, 40g, 45g, 50g, 65g;
Usage: Melting, Assaying;
Refractoriness Under Load: 1420 Degree Celsius;
Packing: Wooden Packing, Paper Carton Packing;
|
Refractoriness (℃): 1580< Refractoriness< 1770;
Feature: Long Time Materials;
Type: Refractory Material;
Shape: Brick;
Material: Magnesia-Hecynite;
Application Area: Sintering Zone in Rotary Kiln;
Size: Customer Made;
Bulk Density: 2.9-2.95g/cm3;
Apparent Porosity: 17%;
Tsr 950ºC: 100 Cycle;
Rul: 1650-1700ºC;
CCS MPa: 60;
|
Refractoriness (℃): Refractoriness> 2000;
Feature: Long Time Materials;
Type: Heat-Resistant Material;
Shape: Powder;
Material: Boron Carbide;
Crystal Color: Black;
Crystal Structure: Rhombi;
Mohs Hardness: 9.36;
Density: More Than 2.52g/cm3;
Flexural Strength: 300-500MPa;
Compressive: 3000-5000MPa;
|
Refractoriness (℃): Refractoriness> 2000;
Feature: Long Time Materials;
Type: Heat-Resistant Material;
Shape: Powder;
Material: Boron Carbide;
Crystal Color: Black;
Crystal Structure: Rhombi;
Mohs Hardness: 9.36;
Density: More Than 2.52g/cm3;
Flexural Strength: 300-500MPa;
Compressive: 3000-5000MPa;
|
Refractoriness (℃): 1580< Refractoriness< 1770;
Feature: Long Time Materials;
Type: Refractory Material;
Shape: Brick;
Material: Synthetic Material;
Application Area: Preheating Zone/Safety Zone;
Bulk Density: 2.2;
Apparent Porosity%: 16;
Tsr: 16 Cycle;
CCS: 57;
Alkali Resistance: 1st Grade;
Size: Customer Made;
|