Specification |
CAS No.: 25035-69-2'7732-18-5;
Formula: 1000;
Color: White;
Solid Content%: 52-54;
Cps: 200-1000;
pH: 6.5-7.5;
Tg: -15;
|
Molecular Principal Chain: Urethane Based Polymer;
Color: White;
Form: Oval Particles;
Hardness,Shore a: -/80~~-/85;
Density,g/cm3: 1.20;
Tensile Strength,MPa: 70-95;
Tear Strength,MPa: 200-220;
Elongation at Break,%: 25-150;
Tg,°c: 90-130;
Flexural Strength,MPa: 115-120;
Flexural Modulus,MPa: 2150-2200;
|
Molecular Principal Chain: Urethane Based Polymer;
Color: White;
Form: Oval Particles;
Hardness,Shore a: 55-95;
Density,g/cm3: 1.19-1.22;
Tensile Strength,MPa: 38-60;
Tear Strength,MPa: 110-220;
Elongation at Break,%: 300-550;
Tg,°c: -42~-30;
100% Modulus,MPa: 5-34;
300% Modulus,MPa: 10-45;
|
Molecular Principal Chain: Urethane Based Polymer;
Color: White;
Form: Oval Particles;
Hardness,Shore a: 55-95;
Density,g/cm3: 1.19-1.22;
Tensile Strength,MPa: 38-60;
Tear Strength,MPa: 110-220;
Elongation at Break,%: 300-550;
Tg,°c: -42~-30;
100% Modulus,MPa: 5-34;
300% Modulus,MPa: 10-45;
|
CAS No.: Not Applicable;
Formula: Not Applicable;
EINECS: Not Applicable;
Molecular Principal Chain: Carbon Chain Polymer;
Color: Transparent;
Appearance: Transparent viscous liquid;
Color,(Fe/Co): 0;
Viscosity, cps. (@60ºC): 30000~40000;
Nco%: <0.1;
Oligomer, wt.%: 100;
Specific Gravity: 1.1496 @ 20C ºC;
Functionality: 4;
|