Specification |
CAS No.: 25035-69-2'7732-18-5;
Formula: 1000;
Color: White;
Solid Content%: 35-37;
pH: 2.0-4.0;
|
CAS No.: Not Applicable;
Formula: Not Applicable;
EINECS: Not Applicable;
Molecular Principal Chain: Carbon Chain Polymer;
Color: Transparent;
Appearance: Transparent viscous liquid;
Color,(Fe/Co): 0;
Viscosity, cps. (@60ºC): 17000~35000;
Nco%: <0.1;
Oligomer, wt.%: 100;
Functionality: 2;
|
CAS No.: 9009-54-5;
EINECS: 210-898-8;
Molecular Principal Chain: Urethane Based Polymer;
Color: White;
Form: Oval Particles;
Hardness,Shore a: 82-96;
Density,g/cm3: 1.12;
100% Modulus,MPa: 7-10;
300% Modulus,MPa: 14-19;
Tensile Strength,MPa: 38-50;
Tear Strength,MPa: 90-130;
Elongation at Break,%: 350-500;
Tear Strength,Kn/M: 90-130;
|
Molecular Principal Chain: Urethane Based Polymer;
Color: White;
Form: Oval Particles;
Hardness,Shore a: -/80~~-/85;
Density,g/cm3: 1.20;
Tensile Strength,MPa: 70-95;
Tear Strength,MPa: 200-220;
Elongation at Break,%: 25-150;
Tg,°c: 90-130;
Flexural Strength,MPa: 115-120;
Flexural Modulus,MPa: 2150-2200;
|
CAS No.: 9009-54-5;
Formula: C3h8n2o;
EINECS: 210-898-8;
Molecular Principal Chain: Urethane Based Polymer;
Color: White;
Form: Oval Particles;
Hardness,Shore a: 55-95;
Density,g/cm3: 1.19-1.22;
Tensile Strength,MPa: 38-60;
Tear Strength,MPa: 110-220;
Elongation at Break,%: 300-550;
Tg,°c: -42~-30;
100% Modulus,MPa: 5-34;
300% Modulus,MPa: 10-45;
|