Specification |
CAS No.: 25035-69-2'7732-18-5;
Formula: 1000;
Color: White;
Solid Content%: 46-48;
Cps: 1800-2700;
pH: 7.0-7.5;
Tg: 18;
|
CAS No.: 26123-45-5;
Formula: C15h14o8;
EINECS: /;
Color: Light Yellow;
|
Molecular Principal Chain: Urethane Based Polymer;
Color: White;
Form: Oval Particles;
Hardness,Shore a: 72-95;
Density,g/cm3: 1.19-1.20;
100% Modulus,MPa: 3-11;
300% Modulus,MPa: 8-26;
Tensile Strength,MPa: 32-50;
Tear Strength,MPa: 90-160;
DIN Abrasion Loss,mm³: 30-35;
|
Molecular Principal Chain: Urethane Based Polymer;
Color: White;
Form: Oval Particles;
Hardness,Shore a: 72-95;
Density,g/cm3: 1.19-1.20;
100% Modulus,MPa: 3-11;
300% Modulus,MPa: 8-26;
Tensile Strength,MPa: 32-50;
Tear Strength,MPa: 90-160;
DIN Abrasion Loss,mm³: 30-35;
|
CAS No.: 9009-54-5;
Formula: C3h8n2o;
Molecular Principal Chain: Urethane Based Polymer;
Color: White;
Form: Oval Particles;
Hardness,Shore a: 83-96;
Density,g/cm3: 1.07-1.14;
100% Modulus,MPa: 5-10;
300% Modulus,MPa: 10-25;
Tensile Strength,MPa: 30-45;
Tear Strength,MPa: 77-120;
Procesing Temperature,°c: 165-180;
|