Specification |
CAS No.: 25035-69-2'7732-18-5;
Formula: 1000;
Color: White;
Solid Content%: 47-49;
Cps: 800-1000;
pH: 6.0-7.5;
Tg: 28;
|
CAS No.: 9009-54-5;
EINECS: 210-898-8;
Molecular Principal Chain: Urethane Based Polymer;
Color: White;
Form: Oval Particles;
Hardness,Shore a: 72-95;
Density,g/cm3: 1.19-1.20;
100% Modulus,MPa: 3-11;
300% Modulus,MPa: 8-26;
Tensile Strength,MPa: 32-50;
Tear Strength,MPa: 90-160;
DIN Abrasion Loss,mm³: 30-35;
|
Molecular Principal Chain: Urethane Based Polymer;
Color: White;
Form: Oval Particles;
Hardness,Shore a: 79-89;
Density,g/cm3: 1.2-121;
Tensile Strength,MPa: 24-30;
Tear Strength,MPa: 75-90;
Elongation at Break,%: 600-800;
Tg ,ºC: -18~-36;
|
CAS No.: 9009-54-5;
EINECS: 210-898-8;
Molecular Principal Chain: Urethane Based Polymer;
Color: White;
Form: Oval Particles;
Hardness,Shore a: 79-89;
Density,g/cm3: 1.2-121;
Tensile Strength,MPa: 24-30;
Tear Strength,MPa: 75-90;
Elongation at Break,%: 600-800;
Tg ,ºC: -18~-36;
|
CAS No.: 9009-54-5;
EINECS: 210-898-8;
Molecular Principal Chain: Urethane Based Polymer;
Color: White;
Form: Oval Particles;
Hardness,Shore a: 83-96;
Density,g/cm3: 1.07-1.14;
100% Modulus,MPa: 5-10;
300% Modulus,MPa: 10-25;
Tensile Strength,MPa: 30-45;
Tear Strength,MPa: 77-120;
Procesing Temperature,°c: 165-180;
|