Specification |
Application: Refractory, Aluminum and Aluminum Alloy;
Feature: Long Time Materials;
Shape: Brick;
Product Name: Alumina Ceramic Foam Filter;
Model No.: Sf-Acf;
Pore Density(Ppi): 10-40;
Porosity(%): 80-90;
Operating Temperature: <1100celsius;
Bending Strength(MPa): >0.6;
Compression Strength(MPa): >0.8;
Thermal Sgock Resistance(Times/1100): 6;
Color: White;
Filter Shape: Square/Round or Custom;
Size: According to Clients Requirements;
Features 1: Effectively Remove The Inclusions;
Features 2: Improve Surface Quality/Product Performance;
Features 3: Improve Microstructure;
Refractoriness (℃): Refractoriness> 2000;
Type: Ablative Material;
Material: Mullite;
|
Application: Refractory;
Feature: Long Time Materials;
Shape: Plate;
Materials: Alumina/ Sic/ Zirconia;
Dimesions: 40*40*22mm, 50*50*22mm, 100*100*22mm, 150*150*22, etc;
Alumina Apllication: Aluminium, Aluminium Alloys;
Sic Apllication: Ductile Cast Iron, Malleable Cast Iron, Gray Irona;
Zirconia Apllication: Steel, Alloy Steel, Stainless Steel;
Alumina Working Temp.: 1200 Degree Centigrade;
Sic Working Temp.: 1560 Degree Centigrade;
Zirconia Working Temp.: 1700 Degree Centigrade;
Porosity: 80-90%;
Pore Density: 8-60ppi;
Volume-Weight: 0.35-0.5 g/cm3;
Bending Strength: >0.8MPa;
Compression Strength: >0.9MPa;
Refractoriness (℃): 1580< Refractoriness< 1770;
Type: Refractory Material;
Material: Silicon Carbide (SiC);
|
Application: Refractory;
Feature: Long Time Materials;
Shape: Plate;
Materials: Alumina/ Sic/ Zirconia;
Dimesions: 40*40*22mm, 50*50*22mm, 100*100*22mm, 150*150*22, etc;
Alumina Apllication: Aluminium, Aluminium Alloys;
Sic Apllication: Ductile Cast Iron, Malleable Cast Iron, Gray Irona;
Zirconia Apllication: Steel, Alloy Steel, Stainless Steel;
Alumina Working Temp.: 1200 Degree Centigrade;
Sic Working Temp.: 1560 Degree Centigrade;
Zirconia Working Temp.: 1700 Degree Centigrade;
Porosity: 80-90%;
Pore Density: 8-60ppi;
Volume-Weight: 0.35-0.5 g/cm3;
Bending Strength: >0.8MPa;
Compression Strength: >0.9MPa;
Refractoriness (℃): 1580< Refractoriness< 1770;
Type: Refractory Material;
Material: Silicon Carbide (SiC);
|
Application: Refractory;
Feature: Long Time Materials;
Shape: Plate;
Refractoriness (ºC): 1770< Refractoriness< 2000;
Types: Types;
Thickness: 12-25mm;
Materials: Sic/Alumina/Zirconia;
Alumina: Alumina or Aluminium Alloy Casting;
Silicon Carbide: Iron or Iron Alloy Casting;
Zirconium Oxide: Steel, Stainless Steel and Synthetic Steel Casting;
Open Porosity(%): 80-90;
Shapes: Rectangle, Round, Square;
Color: White, Gold, Grey Black;
Refractoriness (℃): 1580< Refractoriness< 1770;
Type: Refractory Material;
Material: Silicon Carbide (SiC);
|
Application: Refractory;
Feature: Long Time Materials;
Shape: Plate;
Refractoriness: 1770< Refractoriness< 2000;
Types: Refractory Material;
Thickness: 12-25mm;
Materials: Sic/Alumina/Zirconia;
Alumina: Alumina or Aluminium Alloy Casting;
Silicon Carbide: Iron or Iron Alloy Casting;
Zirconium Oxide: Steel, Stainless Steel and Synthetic Steel Casting;
Open Porosity(%): 80-90;
Shapes: Rectangle, Round, Square;
Color: White, Gold, Grey Black;
Refractoriness (℃): 1580< Refractoriness< 1770;
Type: Refractory Material;
Material: Silicon Carbide (SiC);
|