Specification |
Refractoriness (℃): 1580< Refractoriness< 1770;
Feature: Long Time Materials, Instant Materials;
Type: Refractory Material;
Shape: Brick;
Material: Alumina Block;
Product Name: Ceramic Pouring Cup;
Materials: High Alumina Silicate;
Operating Temperature (ºC): 1650;
Flexural Strength at Room Temperature (M: > 10;
Coefficient of Thermal Expansion: 8~9X10-6;
Application: High Temperature Alloy, Stainless Steel;
|
Refractoriness (℃): 1380;
Feature: Long Time Materials, Instant Materials;
Type: Refractory Material;
Shape: Pipe;
Material: Silicon Carbide (SiC);
Delivery Time: 25-30 Days;
Raw Material: Toner, Silicon Powder;
Application: Industrial Ceramic,Refractory,Industrial Furnaces;
Size: as Customer Need;
Usage: Anti- Strong Acid and Alkali;
Density: More Than 3.02 g/cm3;
Thermal Conductivity: 45 (1200 Celsius);
Moh's Hardness: 9.15;
Vickers Hardness Hv: 20 Gpa;
Open porosity: Less than 0.1%;
Acid alkaline proof: Excellent;
|
Refractoriness (℃): 1380;
Feature: Long Time Materials, Instant Materials;
Type: Refractory Material;
Shape: Pipe;
Material: Silicon Carbide (SiC);
Delivery Time: 25-30 Days;
Raw Material: Toner, Silicon Powder;
Application: Industrial Ceramic,Refractory,Industrial Furnaces;
Size: as Customer Need;
Usage: Anti- Strong Acid and Alkali;
Density: More Than 3.02 g/cm3;
Thermal Conductivity: 45 (1200 Celsius);
Moh's Hardness: 9.15;
Vickers Hardness Hv: 20 Gpa;
Open porosity: Less than 0.1%;
Acid alkaline proof: Excellent;
|
Refractoriness (℃): 1770< Refractoriness< 2000;
Feature: Long Time Materials;
Type: Refractory Material;
Shape: Ball;
Material: MGO;
|
Refractoriness (℃): 1580< Refractoriness< 1770;
Feature: Long Time Materials, Instant Materials, Zero Thermal Expansion Material;
Type: Refractory Material;
Shape: Powder;
Material: Fused Silica;
Sio2: >99.85%;
Fe2o3: <0.01%;
Xrd Test Result: Amorhous;
Density: 2.2g/cm3;
|