Specification |
Refractoriness (℃): 1580< Refractoriness< 1770;
Feature: Long Time Materials, Instant Materials;
Type: Refractory Material;
Shape: Brick;
Material: Alumina Block;
Product Name: Ceramic Pouring Cup;
Materials: High Alumina Silicate;
Operating Temperature (ºC): 1650;
Flexural Strength at Room Temperature (M: > 10;
Coefficient of Thermal Expansion: 8~9X10-6;
Application: High Temperature Alloy, Stainless Steel;
|
Classification: Clay;
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Low Thermal Conductivity, Long Time Materials;
Production Process: Extrusion Method;
Refractoriness (℃): 1580< Refractoriness< 1770, 1770< Refractoriness< 2000;
Shape: Brick, Brick;
Type: Refractory Material;
Material: Alumina Block;
Al2O3: 48%~85%;
Size: Customizable;
Certifiacte: ISO9001, CE, etc;
Refractoriness: Sk35, Sk36, Sk37, Sk38, Sk40;
Apparent Porosity: 20-23%;
Bulk Density: 2.25-2.65g/cm3;
Refractoriness Under [email protected]: 1380-1550;
Thermal Linear Expansion@1000deg: 0.6%;
Fe2o3: 1.8-2.0%;
|
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Low Thermal Conductivity;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Pipe, Ceramic Fiber Tube;
Usage: High Temperature Insulating Material;
Temprature Classification: 1400℃, 1260℃, 1050℃;
Chemical Composition: Al2O3.Sio2, Al2O3+Sio2+Zro2;
Manufacturing Technique: Spray Silk Rug;
Kind: Ordinary Ceramic Fiber;
Bulk Density(g/cm3): 400;
Fiber Diamete: 3-5um;
Thermal Conductivity: 0.075;
Working Temperature: 1050 --1350;
Raw Material: Aluminum Silicate;
Diameter: 5-100mm;
Color: White;
|
Refractoriness (℃): 1580< Refractoriness< 1770;
Feature: Long Time Materials;
Type: Refractory Material;
Shape: Brick;
Material: Magnesia-Alumina;
Standard: VDZ;
SIZE: B622 B322 etc;
Magnesia: 85%;
|
Refractoriness (℃): 1580< Refractoriness< 1770;
Feature: Long Time Materials;
Type: Refractory Material;
Shape: Brick;
Material: Magnesia-Hecynite;
Application Area: transitional Zone in Rotary Kiln;
Size: Customer Made;
Bulk Density: 2.65~2.7g/cm3;
Apparent Porosity: 20 %;
TSR - in water at 1100ºC: 10-15 Cycle;
Refractoriness Under Load: 1650;
CCS MPa: 80-100;
|