Specification |
Application: Refractory, Structure Ceramic, Industrial Ceramic;
Type: Ceramic Plates;
Standard: ISO9001;
Material: Alumina Ceramic;
|
Application: Refractory, Structure Ceramic, Industrial Ceramic;
Type: Ceramic Parts;
Bulk Density: 3.1 Mg/M3;
Porosity: 22% Nominal;
Volum Resistivity: >10^14;
Maximum Use Temperature: 1600;
Flexural Strength: 358;
Thermal Shock Resistance: 200-250;
Processing Service: Moulding;
Thermal Expansion Coefficient: 7.9*10-6/C;
Vickers Hardness: 14gpa;
Flexural Strength(20ºC): Flexural Strength(20ºC);
Compressive Strength(20ºC): 2000MPa;
Thermal Conductivity: 31.5W / (M * K);
Material: Alumina Ceramic;
|
Application: Refractory, Structure Ceramic, Industrial Ceramic;
Purity: 99%;
Type: Ceramic Parts;
Bulk Density: 3.1 Mg/M3;
Porosity: 22% Nominal;
Volum Resistivity: >10^14;
Maximum Use Temperature: 1600;
Flexural Strength: 358;
Thermal Shock Resistance: 200-250;
Processing Service: Moulding;
Thermal Expansion Coefficient: 7.9*10-6/C;
Vickers Hardness: 14gpa;
Flexural Strength(20ºC): Flexural Strength(20ºC);
Compressive Strength(20ºC): 2000MPa;
Thermal Conductivity: 31.5W / (M * K);
Material: Alumina Ceramic;
|
Application: Refractory, Structure Ceramic, Industrial Ceramic;
Type: Ceramic Parts;
Bulk Density: 3.1 Mg/M3;
Porosity: 22% Nominal;
Volum Resistivity: >10^14;
Maximum Use Temperature: 1600;
Flexural Strength: 358;
Thermal Shock Resistance: 200-250;
Processing Service: Moulding;
Thermal Expansion Coefficient: 7.9*10-6/C;
Vickers Hardness: 14gpa;
Flexural Strength(20ºC): Flexural Strength(20ºC);
Compressive Strength(20ºC): 2000MPa;
Thermal Conductivity: 31.5W / (M * K);
Material: Alumina Ceramic;
|
Application: Refractory;
Color: White;Beige;
Shape: Boat,High Form,Arc,Columned,Cylindrical,Tray Ect;
Application Domain: Lab,Molten Industry,Ect;
Property: High Temperature Resistance,Corrosion Resistant;
Accessory: Lid or Cover,Tong;
Volume: 5ml,10ml,100ml,200ml,500ml,1000ml;
Max Temperature: 1800c;
|