Specification |
Application: Electronics, Industrial;
Standard: GB, ASTM;
Purity: 99.95%;
Alloy: Non-alloy;
Type: Molybdenum Bar;
Powder: Not Powder;
Density: 10.2g/cm3;
Surface: Polished;
|
Application: Industrial, Furnace Parts;
Standard: GB, ASTM;
Purity: >99.5%;
Alloy: Alloy;
Type: Rod;
Powder: Not Powder;
Grade: Mhc;
Usage: Hot Processing Tools;
Samples: Available;
Performance: High Temp Resistance;
Hardness: Hv 280-320;
Tensile Strength: 830MPa;
Upper Yield Strength: 786MPa;
Elongation After Fracture: 26%;
|
Application: Industrial, Furnace Parts;
Standard: GB, ASTM;
Purity: >99.95%;
Alloy: Non-alloy;
Type: Parts;
Powder: Not Powder;
Grade: Mo1, Mh1, Mola, Tzm;
Content: Mo 99.95%;
Density: 10.18g/cm3;
Usage: Furnace Parts;
Samples: Available;
Performance: High Temp Resistance;
Hardness: Hv190-230;
|
Application: Industrial, Furnace Parts;
Standard: GB, ASTM;
Purity: >99.5%;
Alloy: Alloy;
Type: Rod;
Powder: Not Powder;
Grade: Mhc;
Usage: Hot Processing Tools;
Samples: Available;
Performance: High Temp Resistance;
Hardness: Hv 280-320;
Tensile Strength: 830MPa;
Upper Yield Strength: 786MPa;
Elongation After Fracture: 26%;
|
Application: Industrial;
Standard: GB;
Purity: >99.95%;
Alloy: Non-alloy;
Type: Molybdenum Wire;
Powder: Not Powder;
Tensile Strength: 850 N/mm2;
Density: 10.2 g/cm3;
|