Specification |
CAS No.: 7085-85-0;
Formula: Mixture;
Bonding Function: Instant Adhesive;
Morphology: Solid-State;
Application: Automobile, Construction, Woodworking, Footwear & Leather, Fiber & Garment, Packing;
Material: Epoxy;
Classification: Room Curing;
Main Agent Composition: Inorganic Adhesive Material;
Characteristic: Waterproof;
Promoter Composition: Curing Agent;
Composition: Organic Material;
Color: Colourful;
Cetificate: ISO, TUV;
OEM: Avaliable;
Shelf Life: 12 Months;
MOQ: 500CTN;
Advantage: Ccaulking Agent Oil Resistance;
|
Bonding Function: Structural Adhesive;
Morphology: Black Paste;
Application: Automobile;
Material: Polyurethane;
Classification: Room Curing;
Main Agent Composition: Polyurethane Prepolymer;
Characteristic: High Viscosity, High Shear Strength, Fast Cure;
Promoter Composition: Complexing Agent;
Composition: Organic Material;
Color: Black;
Density: 1.25±0.05 Kg/L;
Cure Mechanism: Moisture-Curing;
Non-Sag Properties: Good;
Shore a Hardness: ~ 60;
Shear Strength: ≥ 4 N/mm^2;
Tensile Strength: ≥ 7 N/mm^2;
Elongation at Break: ≥ 250%;
Tear Strength: ≥ 10 N/mm;
Tack-Free Time (23 ºC , 50% Rh): 10~20 Min;
Rate of Cure (23 ºC, 50% Rh): ≥ 4 mm/24hrs;
|
Bonding Function: Structural Adhesive;
Morphology: Black Paste;
Application: Automobile;
Material: Polyurethane;
Classification: Room Curing;
Main Agent Composition: Polyurethane Prepolymer;
Characteristic: High Viscosity, High Shear Strength, Fast Cure;
Promoter Composition: Complexing Agent;
Composition: Organic Material;
Color: Black;
Density: 1.25±0.05 Kg/L;
Cure Mechanism: Moisture-Curing;
Non-Sag Properties: Good;
Shore a Hardness: ~ 60;
Shear Strength: ≥ 4 N/mm^2;
Tensile Strength: ≥ 7 N/mm^2;
Elongation at Break: ≥ 250%;
Tear Strength: ≥ 10 N/mm;
Tack-Free Time (23 ºC , 50% Rh): 10~20 Min;
Rate of Cure (23 ºC, 50% Rh): ≥ 4 mm/24hrs;
|
Bonding Function: Structural Adhesive;
Morphology: Black Paste;
Application: Automobile;
Material: Polyurethane;
Classification: Room Curing;
Main Agent Composition: Polyurethane Prepolymer;
Characteristic: High Viscosity, High Shear Strength, Fast Cure;
Promoter Composition: Complexing Agent;
Composition: Organic Material;
Color: Black;
Density: 1.25±0.05 Kg/L;
Cure Mechanism: Moisture-Curing;
Non-Sag Properties: Good;
Shore a Hardness: ~ 60;
Shear Strength: ≥ 4 N/mm^2;
Tensile Strength: ≥ 7 N/mm^2;
Elongation at Break: ≥ 250%;
Tear Strength: ≥ 10 N/mm;
Tack-Free Time (23 ºC , 50% Rh): 10~20 Min;
Rate of Cure (23 ºC, 50% Rh): ≥ 4 mm/24hrs;
|
Bonding Function: Structural Adhesive;
Morphology: Black Paste;
Application: Automobile;
Material: Polyurethane;
Classification: Room Curing;
Main Agent Composition: Polyurethane Prepolymer;
Characteristic: High Viscosity, High Shear Strength, Fast Cure;
Promoter Composition: Complexing Agent;
Composition: Organic Material;
Color: Black;
Density: 1.25±0.05 Kg/L;
Cure Mechanism: Moisture-Curing;
Non-Sag Properties: Good;
Shore a Hardness: ~ 60;
Shear Strength: ≥ 4 N/mm^2;
Tensile Strength: ≥ 7 N/mm^2;
Elongation at Break: ≥ 250%;
Tear Strength: ≥ 10 N/mm;
Tack-Free Time (23 ºC , 50% Rh): 10~20 Min;
Rate of Cure (23 ºC, 50% Rh): ≥ 4 mm/24hrs;
|