| Specification |
Classification: High-Alumina;
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant;
Production Process: Extrusion Method;
Refractoriness (℃): 1770< Refractoriness< 2000;
Shape: Block;
Product Name: Ladle Sliding Gate Plate Refractory CCM;
Al2O3: 85% Min;
Apparent Porosity: 15%;
Bulk Density: 3GM./Cc Min;
C.C.S: 100MPa Min;
Application: Steel Mill Ladle;
Mould: According to The Customer′s Request;
Function: Flow Control;
Drawing: Customized;
Chemical Physical Analysis: Customized;
Sample Order: Acceptable;
Main Material: Tabular Alumina, Carbonaceous Material;
Zirconia: Can Be Added;
Used for: Steel Making Molten Melting;
Color: Black;
|
Classification: Alloy;
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Low Thermal Conductivity, Long Time Materials;
Production Process: Casting Method;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Pipe;
Raw Material: Alloy;
Bulk Density: 2.7 g/cm3;
Apparent Porosity: 5~18%;
Certifiacte: ISO9001, CE, etc;
Feature 2: High Hardness, High Thermal Shoc;
Application: Steel Industry;
Thermal Shock Resistance: Excellent;
Classification Temperature: 1500-1800 ºC;
Color: Blank, Grey;
Size Control: Accurate;
Production Time: 15-30 Days;
Testing Laboratory: Support;
|
Classification: Silicon Carbide (Sic);
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Low Thermal Conductivity, Long Time Materials;
Production Process: Casting Method;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Pipe;
Raw Material: Alloy;
Bulk Density: 2.7 g/cm3;
Apparent Porosity: 5~18%;
Certifiacte: ISO9001, CE, etc;
Feature 2: High Hardness, High Thermal Shoc;
Application: Steel Industry;
Thermal Shock Resistance: Excellent;
Classification Temperature: 1500-1800 ºC;
Color: Blank, Grey;
Size Control: Accurate;
Production Time: 15-30 Days;
Testing Laboratory: Support;
|
Classification: Alloy;
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Low Thermal Conductivity, Long Time Materials;
Production Process: Casting Method;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Pipe;
Raw Material: Alloy;
Bulk Density: 2.7 g/cm3;
Apparent Porosity: 5~18%;
Certifiacte: ISO9001, CE, etc;
Feature 2: High Hardness, High Thermal Shoc;
Application: Steel Industry;
Thermal Shock Resistance: Excellent;
Classification Temperature: 1500-1800 ºC;
Color: Blank, Grey;
Size Control: Accurate;
Production Time: 15-30 Days;
Testing Laboratory: Support;
|
Classification: High-Alumina;
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Low Thermal Conductivity;
Refractoriness (℃): 1770< Refractoriness< 2000;
Shape: Powder;
Bulk Density g/cm3: 3.3G/Cm3;
A1203: 0.2%;
Fe2o3: 0.8%;
Raw Material: Magnesite;
|