Specification |
Classification: High-Alumina;
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Low Thermal Conductivity;
Production Process: Sintering Method;
Refractoriness (℃): 1770< Refractoriness< 2000;
Shape: Plate;
Product Name: Ladle Refractories Sliding Gate Plates for Steel M;
Al2O3: 80% Min;
Apparent Porosity: 15%;
Bulk Density: 3GM./Cc Min;
C.C.S: 100MPa Min;
Application: Steel Mill Ladle;
Mould: According to The Customer's Request;
Hot Sales Area: Pakistan;
Function: Flow Control;
Drawing: Customized;
Chemical Physical Analysis: Customized;
Sample Order: Acceptable;
Service Life: 4-8 Heats;
Main Material: Tabular Alumina, Carbonaceous Material;
Zirconia: Can Be Added;
|
Feature: Long Time Materials;
Refractoriness (℃): 1770< Refractoriness< 2000;
Shape: Funnel, Sleeve, Round and Square Tube, Spider;
Application: Fourdry Industry Bottom Poring System;
Bulk Density: 2100-2350 Kg/M3;
Features: Low Sticking of Refractory and Steel After Use;
Cold Crushing Strength: 30 - 40 MPa;
Type: Molten Steel Pouring Control Material;
Material: Flint Clay, Bauxite, Andalusite, Mullite;
|
Feature: Long Time Materials;
Refractoriness (℃): 1770< Refractoriness< 2000;
Shape: Brick, Funnel, Sleeve, Round and Square Tube, Spider, etc.;
Application: Fourdry Industry Cast Iron/Bottom Pouring System;
Bulk Density: 2100-2350 Kg/M3;
Features: Low Sticking of Refractory and Steel After Use;
Cold Crushing Strength: 30 - 40 MPa;
Type: Molten Steel Pouring Control Material;
Material: Flint Clay, Bauxite, Andalusite, Mullite;
|
Feature: Long Time Materials;
Refractoriness (℃): 1770< Refractoriness< 2000;
Shape: Brick, Funnel, Sleeve, Round and Square Tube, Spider, etc.;
Application: Fourdry Industry Bottom Pouring System;
Bulk Density: 2100-2350 Kg/M3;
Features: Low Sticking of Refractory and Steel After Use;
Cold Crushing Strength: 30 - 40 MPa;
Type: Molten Steel Pouring Control Material;
Material: Flint Clay, Bauxite, Andalusite, Mullite;
|
Feature: Long Time Materials;
Refractoriness (℃): 1770< Refractoriness< 2000;
Shape: Block, Funnel, Sleeve, Round and Square Tube, Spider, etc.;
Application: Fourdry Industry Bottom Pouring System;
Bulk Density: 2100-2350 Kg/M3;
Features: Low Sticking of Refractory and Steel After Use;
Cold Crushing Strength: 30 - 40 MPa;
Type: Molten Steel Pouring Control Material;
Material: Flint Clay, Bauxite, Andalusite, Mullite;
|