| Specification |
Classification: High-Alumina;
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Low Thermal Conductivity;
Production Process: Sintering Method;
Refractoriness (℃): 1770< Refractoriness< 2000;
Shape: Plate;
Product Name: Impregnated Tempered Ladle Slide Gate Plate for St;
Al2O3: 85% Min;
Apparent Porosity: 15%;
Bulk Density: 3GM./Cc Min;
C.C.S: 100MPa Min;
Application: Steel Mill Ladle;
Mould: According to The Customer's Request;
Hot Sales Area: Pakistan;
Function: Flow Control;
Drawing: Customized;
Chemical Physical Analysis: Customized;
Sample Order: Acceptable;
Service Life: 4-8 Heats;
Main Material: Tabular Alumina, Carbonaceous Material;
Zirconia: Can Be Added;
|
Feature: Light Weight, Long Time Materials;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Brick;
Product Name: Mullite Insulation Bircks;
Cold Compressive Strength: 1.2-2.5 MPa;
Bulk Density: 0.55-1.03 g/cm3;
Fe2o3: Max 1.0%;
Softening Temperature Under Load: More Than 1420;
Apparent Porosity (%): More Than 62%;
Usage: Glass Furnace, Steel Converter .etc;
Price: Factory Outlets;
Keyword: Light Weight Insulation Mullite Bricks Sta;
Samples: Provide;
Keyword 1: Insulation Brick;
Type: Refractory Material;
Material: Mullite;
|
Feature: Long Time Materials;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Brick;
Product Name: Mullite Insulation Bircks;
Cold Compressive Strength: 1.2-2.5 MPa;
Bulk Density: 0.55-1.03 g/cm3;
Fe2o3: Max 1.0%;
Softening Temperature Under Load: More Than 1420;
Apparent Porosity (%): More Than 62%;
Usage: Glass Furnace, Steel Converter .etc;
Price: Factory Outlets;
Keyword: Light Weight Insulation Mullite Bricks Sta;
Samples: Provide;
Keyword 1: Insulation Brick;
Type: Refractory Material;
Material: Mullite;
|
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Light Weight, Low Thermal Conductivity;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Module;
Usage: High Temperature Insulating Material;
Temprature Classification: 1400c, 1260c;
Chemical Composition: Al2O3.Sio2;
Manufacturing Technique: Spray Silk Rug;
Kind: Ordinary Ceramic Fiber;
Classification Temperature: 1260c;
Certifiacte: ISO9001:2000;
Bulk Density: 160-220 Kg/Cm3;
Al2O3: 44%;
Sio2: 52%;
Fe2o3+TiO2: 1.0%;
Thermal Conductivity@400c: 0.09W/M.K;
Thermal Conductivity@500c: 0.119W/M.K;
Thermal Conductivity@600c: 0.152W/M.K;
Linear Shrinkage After Heating: 2.5%@1000c*24h;
|
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Light Weight, Low Thermal Conductivity;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Module;
Usage: High Temperature Insulating Material;
Temprature Classification: 1400c, 1260c;
Chemical Composition: Al2O3.Sio2;
Manufacturing Technique: Spray Silk Rug;
Kind: Ordinary Ceramic Fiber;
Classification Temperature: 1260c;
Certifiacte: ISO9001:2000;
Bulk Density: 160-220 Kg/Cm3;
Al2O3: 44%;
Sio2: 52%;
Fe2o3+TiO2: 1.0%;
Thermal Conductivity@400c: 0.09W/M.K;
Thermal Conductivity@500c: 0.119W/M.K;
Thermal Conductivity@600c: 0.152W/M.K;
Linear Shrinkage After Heating: 2.5%@1000c*24h;
|