Specification |
Material: Steel;
Usage: Grind;
Size: Big;
Customized: Customized;
Used for: Ball Mills for Mines/Cememt;
Diameter: 40-150mm;
Hardness: High;
Made of: Cast Steel and Forged Steel;
|
Material: Chromium;
Content: 1-16%;
Usage: Construction, Machinery, Chemical, Petroleum, Grind, Refractory Material, Mines;
Processing Type: Casting;
Size: 17-120mm;
Color: Black;
Customized: Customized;
Process: Casting;
Good Wear Rate: Strong Microscopic Structure;
Heat Treatment: Oil Quenching+Tempering;
Hardness: 45-66HRC;
Broken Rate: <0.5%;
Advantage: Long Service Life & Good Wear Resistence;
|
Material: Chromium;
Content: 1-16%;
Usage: Construction, Machinery, Chemical, Petroleum, Grind, Refractory Material, Mines;
Processing Type: Casting;
Size: 17-120mm;
Color: Black;
Customized: Customized;
Process: Casting;
Good Wear Rate: Strong Microscopic Structure;
Heat Treatment: Oil Quenching+Tempering;
Hardness: 45-66HRC;
Broken Rate: <0.5%;
Advantage: Long Service Life & Good Wear Resistence;
|
Material: Tc, Hard Metal, Hard Alloy, Tungsten Steel;
Content: Wc92%+Co8%;
Usage: Ball Mill, Roller Jar Mill, Attritors, Shaker Mill;
Processing Type: Sintering;
Size: 4,5,6,8,10,12,14,16,18,20mm etc. in Stock;
Color: Metallic;
Customized: Accepted;
Grade: Tungsten Carbide Mc8;
Grain Size: 1.2-1.6 μm;
Density: 14.7-14.78g/Cm³;
Hardness: 89.5-90.5hra;
Trs: >2300MPa;
Surface Finish: Unground;
Features: Resistant to Wear Corrosion and Impact;
|
Material: Chromium;
Content: 1-16%;
Usage: Construction, Machinery, Chemical, Petroleum, Grind, Refractory Material, Mines;
Processing Type: Casting;
Size: 17-120mm;
Color: Black;
Customized: Customized;
Process: Casting;
Good Wear Rate: Strong Microscopic Structure;
Heat Treatment: Oil Quenching+Tempering;
Hardness: 45-66HRC;
Broken Rate: <0.5%;
Advantage: Long Service Life & Good Wear Resistence;
|