Specification |
Exclusion Range (Globular Proteins), Da: 10000-4*10 6;
Particle Size (μm): 45-165;
Max. Flow Rate (Cm/H): 240;
Max. Pressure (MPa): 0.1;
pH Stability: 3-13 (Opeartional) 2-14 (CIF);
Chemical Resistance: Refer to The Table Below;
|
Molecular Principal Chain: Urethane Based Polymer;
Color: White;
Form: Oval Particles;
Hardness,Shore a: 79-89;
Density,g/cm3: 1.2-121;
Tensile Strength,MPa: 24-30;
Tear Strength,MPa: 75-90;
Elongation at Break,%: 600-800;
Tg ,ºC: -18~-36;
|
CAS No.: 9009-54-5;
EINECS: 210-898-8;
Molecular Principal Chain: Urethane Based Polymer;
Color: White;
Form: Oval Particles;
Hardness,Shore a: 79-89;
Density,g/cm3: 1.2-121;
Tensile Strength,MPa: 24-30;
Tear Strength,MPa: 75-90;
Elongation at Break,%: 600-800;
Tg ,ºC: -18~-36;
|
CAS No.: 9009-54-5;
EINECS: 210-898-8;
Molecular Principal Chain: Urethane Based Polymer;
Color: White;
Form: Oval Particles;
Hardness,Shore a: 83-96;
Density,g/cm3: 1.07-1.14;
100% Modulus,MPa: 5-10;
300% Modulus,MPa: 10-25;
Tensile Strength,MPa: 30-45;
Tear Strength,MPa: 77-120;
Procesing Temperature,°c: 165-180;
|
CAS No.: 9009-54-5;
Formula: C3h8n2o;
Color: White;
Form: Oval Particles;
Hardness,Shore a: 75-82;
Density,g/cm3: 1.19-1.22;
100% Modulus,MPa: 5-35;
300% Modulus,MPa: 12-43;
Tensile Strength,MPa: 35-60;
Tear Strength,MPa: 100-240;
Procesing Temperature,°c: 165-180;
|