Specification |
Application: Wall/Roof Covering Cloth, Filter Cloth, Fiberglass Mesh Cloth, Blind, Fabrics for High Temperature Machine;
Surface Treatment: PTFE Coated;
Weave Type: Plain Woven;
Fiberglass Type: E-Glass;
Alkali Content: Alkali Free;
Type: PTFE Coated Fiberglass Fabric/Cloth;
Weight: 200G/M-2000G/M;
Thickness: 0.2mm~5mm, or Customized;
Standing Temperature: -70-260c;
Color: Grey, Brown, Black ,Green;
Good Features: High Temperature,Abrasion,Water,Chemical Resist;
Application 1: Non-Stick Liners to Resist High Temperature;
Application 2: Conveyor Belts, Fusing Belts, Sealing Belts;
Application 3: Covering or Wrapping Materal;
Application 6: Wrapping High Temperature Resistance Material;
Application 5: Petroleum, Power, Electrical , Chemical Industries;
|
Application: Wall/Roof Covering Cloth, Filter Cloth, Fiberglass Mesh Cloth, Blind;
Surface Treatment: Silicon Coated;
Weave Type: Plain Woven;
Fiberglass Type: E-Glass;
Alkali Content: Alkali Free;
Product Name: Silicone Coated Fiberglass Cloth;
Color: White Grey Red;
Standing Temperature: -70-260ºC;
Thickness: 0.4mm-1mm;
Good Features: Heat Resistane, Electricity, Anti-Corrosion;
|
Application: Widely Used in Industries Such as Packaging, Heat;
Surface Treatment: PTFE Coated;
Weave Type: Plain Woven;
Fiberglass Type: E-Glass;
Alkali Content: Alkali Free;
Product Name: PTFE Adhesive Tape;
Thickness: 0.13mm, 0.18mm, 0.2mm, 0.3mm, 0.4mm;
Adhesive Side: Single Sided;
Width: 5-1250mm;
Temperature: -70-260ºC;
Feature: High Temperature Resistance, Not Sticky, and Vario;
|
Application: Widely Used in Industries Such as Packaging, Heat;
Surface Treatment: PTFE Coated;
Weave Type: Plain Woven;
Fiberglass Type: E-Glass;
Alkali Content: Alkali Free;
Product Name: PTFE Adhesive Tape;
Thickness: 0.13mm, 0.18mm, 0.2mm, 0.3mm, 0.4mm;
Adhesive Side: Single Sided;
Width: 5-1250mm;
Temperature: -70-260ºC;
Feature: High Temperature Resistance, Not Sticky, and Vario;
|
Application: Wall/Roof Covering Cloth;
Surface Treatment: Coated with PU;
Weave Type: Plain Woven;
Fiberglass Type: E-Glass;
Alkali Content: Alkali Free;
Total Weight: 230GSM+/-5%;
Coating Weight: 15~20GSM/ 2side;
Thickness: 0.20+/-0.02mm;
Working Temperature: -70~120 Degrees;
Thermal Conductivity: 1.0W/Mk;
Tensile Strength: >/=1400/1000n/5cm;
Tearing Strength: >/=105/110n;
|