| Specification |
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Light Weight, Low Thermal Conductivity;
Production Process: Extrusion Method;
Refractoriness (℃): 1770< Refractoriness< 2000;
Shape: Brick;
Modelnumber: Jm;
Crushing Strength: 1.2MPa;
Keyword: Insulating Corundum Mullite Fire Brick;
Cao Content %: 0.01;
MGO Content (%): 0.18%;
Refractoriness (Degree): Common1580<Refractoriness<1770;
Bulk Density: 0.6g/cm3;
Single Package Size: 100X100X110.Cm;
Sic Content (%): 1.2%~1.4%;
Modulus of Rupture: 1.Ompa;
Al203 Content %): 40%;
Apparent Porosity: 20-23%;
Cro Content (%): 0.1~0.3%;
Application: Refractory Industry;
|
Classification: High-Alumina;
Feature: Good Mechanical Strength, High-Temperature Resistant;
Production Process: Deep Fired;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Plate;
Product Name: Ladle Bottom Well Block Nozzle Slide Gate Plate Fo;
Materials: Al2O3 Zro2 C or Al C;
Al2O3: 85% Min;
Zro2: 4% Min;
C: 3% Min;
Fire Process: Burned;
Finish Product: with Steel Can and Belt;
Semi-Finished Products: Available;
Rough Brick: Available;
Application: Continuous Casting Flow Control;
Usage Area: Steel Iron Industry;
Function: Control The Flow Rate of Molten Steel;
Type: Steel Making Ladle Bottom Refractory;
Slide Gate Mechansim: Available;
Service Life Performance: 4-8 Times;
|
Feature: Long Time Materials, Instant Materials, Hot Products;
Refractoriness (℃): Refractoriness> 2000;
Shape: Ball;
Product Name: High Alumina Refractory Ball;
Sio2 Content (%): 50%~65%;
Al2O3 Content (%): 65%~95%;
MGO Content (%): 0.8-1.2;
Cao Content (%): 0.34%;
Refractoriness (Degree): Super-Class (Refractorines;
Cro Content (%): 0.002%;
Sic Content (%): 1.2-1.4;
Model Number: Refractory Balls, Customer's Requirem;
Cold Crushing Strength(MPa): 13~36;
Application: Insulation Furnace;
Bulk Density(g/cm3): 2.3~3.1;
Size(mm): 40-80mm;
Apparent Porosity(%): 25~18;
Thermal Shock Resistance: 7~20;
Type: Refractory Material;
Material: Alumina Block;
|
Classification: Al-Zr-C;
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Light Weight, Low Thermal Conductivity;
Production Process: Extrusion Method;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Plate;
Feature 1: High Temperature Resistance;
Feature 2: Good Wear Resistance;
Feature 3: Precise Control Performance;
Use Area: Slide Gate Valve in Steel Making;
Function: Control The Flow of Molten Steel in Continuous;
Main Material: Alumina, Carbonaceous Material;
Sample Order: Acceptable;
|
Classification: High-Alumina;
Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Low Thermal Conductivity;
Production Process: Stirring Processing;
Refractoriness (℃): 1580< Refractoriness< 1770;
Shape: Powder;
Item: Low Cement Castable;
Bulk Density: 2.2-2.7 g/cm3;
Color: Grey, White;
Application: Industrial Furnaces;
Advantage: High Temperature Resistant;
Service Tempera: 1200-1700 ºC;
Cold Crushing Strength: 40-80 MPa;
Chemical Analysis: Al2O3/Cao/Fe2o3;
Production Time: 15-30 Days;
Customized: Acceptable;
Testing Laboratory: Support;
Thermal Shock Resistance: Excellent;
Quality Assurance: Yes;
Performance: Excellent;
|